지각과민억제제 적용이 수종 접착제의 미세인장결합강도에 미치는 영향

Abstract

This study evaluated the influence of a desensitizer(MS coat) on microtensile bond strength of different adhesives: a three-step adhesive(All-Bond 2), a two-step adhesive(Single Bond), a one-step adhesive(One-up Bond F)Non-caries extracted human molars were used. Dentin surface was obtained by horizontal section on mid-portion of crown using a water-cooled low speed diamond saw. Teeth were randomly divided into 6 group. AMO(MS coat + All Bond)-, SMO(MS coat + Single Bond)- and OMO(MS coat + One-up Bond F)-dentin surface were treated with 17% EDTA before bonded adhesive. AMX-, SMX- and OMX-dentin surface were bonded with All-Bond 2, Single Bond and One-up Bond F, respectively, with no previous treatment with MS coat and 17% EDTA. About 1cm high resin composite(Z-250TM) were incrementally build-up on the treated surface. The specimens for the microtensile test were serially sectioned perpendicular to the adhesive layer to obtain 0.7×0.7 mm sticks. 30 sticks were prepared from each group.After that, tensile bond strength for each stick was measured with Microtensile Tester at a 1mm/min crosshead speed. Fractured dentin surfaces were observed under the SEM. The results were statistically analysed by using a One-way ANOVA and Tukey's test(p<0.05).