광중합형 구치부 수복재료의 중합 수축력과 교두 변위의 상관관계
Measurements of shrinkage stress and reduction of inter-cuspal distance in maxillary premolars resulting from polymerization of composites and compomers
1
조회
0
다운로드
1
인용
0
참고문헌
초록
Abstract
The purpose of present study was to evaluate the polymerization shrinkage stress and cuspal deflection in maxillary premolars resulting from polymerization shrinkage of composites and compomers. Composites and compomers which were used in this study were as follows: Dyract AP, Z100, Surefil, Pyramid, Synergy Compact, Heliomolar, Heliomolar HB, and Compoglass F. For measuring of polymerization shrinkage stress, Stress measuring machine(R&B, Daejon, Korea) was used. One-way ANOVA analysis with Duncan's multiple comparison test were used to determine significant differences between the materials. For measuring of cuspal deflection of tooth, MOD cavities were prepared in 10 extracted maxillary premolars. And reduction of intercuspal distance was measured by strain measuring machine (R&B, Daejon, Korea) One-way ANOVA analysis with Turkey test were used to determine significant differences between the materials. Polymerization shrinkage stress is『Heliomolar, Z100, Pyramid < Synergy Compact Compoglass F < Dyract AP < Heliomolr HB, surefil』 (P < 0.05). And cuspal delfelction is『Z100, Heliomolar, Heliomolar HB, Synergy Compact Surefil, < Compoglass F < Pyramid, Dyract AP』 (P < 0.05). Measurements of ploymerization shrinkage stress and those of cuspal deflection of the teeth was different. There is no correlation between polymerization shrinkage stress and cuspal deflection of the teeth. (p > 0.05)
참고문헌 (18)
- "Clinical significance of polymerization shrinkage of composite resins", pp.59~67
- "Polymerization shrinkage of posterior composites resins and its possible influence on postoperative sensitivity", 17, pp.103~111 (1986)
- "Marginal sealing of curing contractions gaps in class V composite resin restorations", 67, pp.841~845 (1988)
- "Fracture toughness of composite and unfilled restorative resins", pp.748~
- "Setting stress in composite resin in relation to configuration of the restoration", pp.1636~1639
- "Increased wall to wall curing contraction in thin bonded resin layers", pp.50~58 (1989)
- "Effect of cavity depth and application technique on marginal adaptation of resins in dentin cavities", 65(11), pp.1319~1321 (1986)
- "A three-sited light curing technique for conventional Class II composite restoraions", pp.125~131
- "The importance of proximal curing in posterior composite resin restorations", pp.605~609
- "Marginal adaptation of class V restorations using different restorative technique", pp.24~32
- "In vitro studies of cuspal movement produced by adhesive materials", pp.405~409
- "Consistency in the amount of linear polymerization shrinkage in syringe type composite", pp.442~446 (1999)
- "A comparison of microhardness of resin composites polymerized by plasma arc or conventional visible light curing", 27, pp.30~37 (2002)
- "Cusp movement in premolars resulting from composite polymerization shrinkage", pp.6~10
- "Reduction of cusp deflection resulting from composite polymerization shrinkage", pp.244~248 (1994)
- "Amount of polymerization shrinkage stress in composites and compomers for posterior restoration", 28, pp.354~ (2003)
- "Reduction of polymerization contraction stress for dental composites by two-step light activation", 18, pp.436~444 (2002)
- "The polymerization shrinkage of composite resins", 5, pp.41~44 (1989)