니켈티타늄 전동 파일의 기계적 특성 비교: Aurum Blue vs. Aurum Pro
Comparison of mechanical properties of nickel-titanium rotary files: Aurum Blue vs. Aurum Pro
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
AIM: The purpose of this study was to evaluate and compare the torsional fracture resistances, cyclic fatigue resistance, and bending stiffness of two nickel-titanium (NiTi) rotary instruments made of different heat-treated alloy: Aurum Blue (heat-treated) and Aurum Pro (conventional). Methods: Forty-five Aurum Blue and Aurum Pro NiTi files were selected for the three mechanical tests (n=15). For the torsional resistance test, 3 mm file tip was fixed and the shaft was driven clockwise at 2 rpm until fracture occurred by using a customized device. Cyclic fatigue resistance was evaluated by rotating instruments in artificial canal with dynamic mode. Bending stiffness was tested by observation of the bending moment on attaining a 45° bend. The results were analyzed by student-t tests at a significance level of 95%. The fractured surface of each groups were examined under a scanning electron microscope (SEM). Results: Aurum Blue showed significantly higher toughness, ultimate strength, distortion angle, and number of cycles to failure than those of Aurum Pro (p < 0.05). However, Aurum Blue and Aurum Pro did not differ significantly in terms of bending stiffness. SEM showed typical topographic appearances of the cyclic fatigue and torsional fracture. Conclusions: Under the limitations of this study, heat-treated instruments showed higher flexibility and fracture resistances than conventional NiTi instruments.
Abstract
AIM: The purpose of this study was to evaluate and compare the torsional fracture resistances, cyclic fatigue resistance, and bending stiffness of two nickel-titanium (NiTi) rotary instruments made of different heat-treated alloy: Aurum Blue (heat-treated) and Aurum Pro (conventional). Methods: Forty-five Aurum Blue and Aurum Pro NiTi files were selected for the three mechanical tests (n=15). For the torsional resistance test, 3 mm file tip was fixed and the shaft was driven clockwise at 2 rpm until fracture occurred by using a customized device. Cyclic fatigue resistance was evaluated by rotating instruments in artificial canal with dynamic mode. Bending stiffness was tested by observation of the bending moment on attaining a 45° bend. The results were analyzed by student-t tests at a significance level of 95%. The fractured surface of each groups were examined under a scanning electron microscope (SEM). Results: Aurum Blue showed significantly higher toughness, ultimate strength, distortion angle, and number of cycles to failure than those of Aurum Pro (p < 0.05). However, Aurum Blue and Aurum Pro did not differ significantly in terms of bending stiffness. SEM showed typical topographic appearances of the cyclic fatigue and torsional fracture. Conclusions: Under the limitations of this study, heat-treated instruments showed higher flexibility and fracture resistances than conventional NiTi instruments.
참고문헌 (18)
- Thompson SA, "An overview of nickel-titanium alloys used in dentistry", Int Endod J, 33, pp.297~310 (2000)
- Peters OA, "Current challenges and concepts in the preparation of root canal systems : a review", J Endod, 30, pp.559~567 (2004)
- Sattapan B, "Defects in rotary nickel-titanium files after clinical use", J Endod, 26, pp.161~165 (2000)
- Parashos P, "Factors influencing defects of rotary nickel-titanium endodontic instruments after clinical use", J Endod, 30, pp.722~725 (2004)
- Shen Y, "Current challenges and concepts of the thermomechanical treatment of nickel-titanium instruments", J Endod, 39, pp.163~172 (2013)
- Shen Y, "Three-dimensional analysis of cutting behavior of nickel-titanium rotary instruments by microcomputed tomography", J Endod, 34, pp.606~610 (2008)
- Elnaghy AM, "Mechanical properties of ProTaper Gold nickel-titanium rotary instruments", Int Endod J, 49, pp.1073~1078 (2016)
- Yum J, "Torsional strength and toughness of nickel-titanium rotary files", J Endod, 37, pp.382~386 (2011)
- Alapati SB, "SEM Observations of nickel-titanium rotary endodontic instruments that fractured during clinical use", J Endod, 31, pp.40~43 (2005)
- Xu X, "Comparative study of torsional and bending properties for six models of nickel-titanium root canal instruments with different cross-sections", J Endod, 32, pp.372~375 (2006)
- Park SY, "Dynamic torsional resistance of nickel-titanium rotary instruments", J Endod, 36, pp.1200~1204 (2010)
- Wycoff RC, "An in vitro comparison of torsional stress properties of three different rotary nickel-titanium files with a similar cross-sectional design", J Endod, 38, pp.1118~1120 (2012)
- Goo HJ, "Mechanical properties of various heat-treated nickel-titanium rotary instruments", J Endod, 43, pp.1872~1877 (2017)
- Santos Lde A, "Comparison of the mechanical behavior between controlled memory and superelastic nickel-titanium files via finite element analysis", J Endod, 39, pp.1444~1447 (2013)
- Topçuoğlu HS, "Effect of two different temperatures on resistance to cyclic fatigue of one Curve, EdgeFile, HyFlex CM and ProTaper next files", Aust Endod J (2019)[DOI]
- Rubio J, "A comparative study of cyclic fatigue of 10 different types of endodontic instruments : an in vitro study", Acta Stomatol Croat, 53, pp.28~36 (2019)
- Zupanc J, "New thermomechanically treated NiTi alloys-a review", Int Endod J, 51, pp.1088~1103 (2018)
- Pedullà E, "Shaping ability of two nickel-titanium instruments activated by continuous rotation or adaptive motion: a micro-computed tomography study", Clin Oral Investig, 20, pp.2227~2223 (2016)