Effect of Spray-drying Condition and Surfactant Addition on Morphological Characteristics of Spray-dried Nanocellulose
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this study, spray-drying yield and morphological characterization of spray-dried cellulose nanofibril (CNF) and TEMPO-oxidized nanocellulose (TONC) depending on spray-drying condition and surfactant addition was investigated. As spray-drying temperature increased, the yield of spray-dried CNF was increased. The highest spray-drying yields in both nanocelluloses were found at didecyl dimethyl ammonium chloride (DDAC) addition of 2.5 phr at all investigated temperatures. The spray-dried CNF was the sphere-like particle, but the spray-dried TONC showed both rod and sphere-like morphology. The average diameter of spray-dried CNF was decreased with increasing DDAC addition amount, resulting in the increase of specific surface area.
Abstract
In this study, spray-drying yield and morphological characterization of spray-dried cellulose nanofibril (CNF) and TEMPO-oxidized nanocellulose (TONC) depending on spray-drying condition and surfactant addition was investigated. As spray-drying temperature increased, the yield of spray-dried CNF was increased. The highest spray-drying yields in both nanocelluloses were found at didecyl dimethyl ammonium chloride (DDAC) addition of 2.5 phr at all investigated temperatures. The spray-dried CNF was the sphere-like particle, but the spray-dried TONC showed both rod and sphere-like morphology. The average diameter of spray-dried CNF was decreased with increasing DDAC addition amount, resulting in the increase of specific surface area.
참고문헌 (5)
- Abe K, "Obtaining cellulose nanofibers with a uniform width of 15 nm from wood", Biomacromolecules, 8, pp.3276~3278 (2007)
- Henriksson M, "Cellulose nanopaper structures of high toughness", Biomacromolecules, 9, pp.1579~1585 (2008)
- Iwamoto S, "The effect of hemicelluloses on wood pulp nanofibrillation and nanofiber network characteristics", Biomacromolecules, 9, pp.1022~1026 (2008)
- Peng Y, "Drying cellulose nanofibrils : in search of a suitable method", Cellulose, 19, pp.91~102 (2012)
- Peng Y, "Spray-drying cellulose nanofibrils : effect of drying process parameters on particle morphology and size distriution", Wood and Fiber Science, 44, pp.1~14 (2012)