인계 폴리올을 이용한 난연성 폴리우레탄의 합성 및 특성 분석
Synthesis and Characterization of Phosphorus Polyurethanes Using Phosphorus Polyols
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
본 연구에서는 인계 폴리올을 phenylphosphonic dichloride (PPDC), allylphosphonic dichloride (APDC)에 ethylene glycol (EG)을 반응시켜 합성하였고 분자량이 880∼1,560 g/mol의 폴리올 얻었다. 이를 이용하여 polycarbonate diol (PCD)와 함께 4,4’-diphenylmethane diisocyanate (MDI)와 중합하여 인계 폴리우레탄을 얻었다. 합성한 인계 폴리우레탄의 인의 합량이 높아질수록 열분해 온도는 감소하였지만 챠 (char)의 발생과 발생양이 증가하는 것을 확인하였다. 또한 UL-94V 시험법을 통하여 APDC를포함하는 인계 폴리우레탄 인의 함유량이 0.5 wt%이상일 때 V-0의 난연등급되는 것을 확인하였다
Abstract
In this study, phosphorus polyols, having a molecular weight of 880 to 1,560 g/mol, were synthesized by reacting phenylphosphonic dichloride (PPDC), allylphosphonic dichloride (APDC), and ethylene glycol (EG) in solvent, to enhance flame retardance of polyurethane. Phosphorus polyurethanes were polymerized using the synthesized phosphorus polyols, polycarbonate diol (PCD), and 4,4’-diphenylmethane diisocyanate (MDI) by a melt polymerization method. As increasing phosphorus contents of the phosphorus polyurethanes, we observed that the remaining char amount increased. This tendency was also confirmed in the following UL-94V test. We found that when the synthesized phosphorus polyols were applied, the resulting phosphorus polyurethanes show UL-94V0 grade at above 0.5 wt% phosphorus contents.
참고문헌 (14)
- S. Monge, , Biomacromolecules, 12, pp.1973~ (2011)
- T. Bock, , Macromol. Rapid Commun, 27, pp.2065~ (2006)
- S. V. Kotov, , J. Flu. Chem, 82, pp.13~ (1997)
- F. Jiang, , Macromolecules, 41, pp.3081~ (2008)
- K. N. Bauer, , Prog. Polym. Sci, 73, pp.61~ (2017)
- B. N. Jang, , Polym. Sci. Technol, 20, pp.8~ (2009)
- M. M. Velencoso, , Angew. Chemie – Int. Ed, 57, pp.10450~ (2018)
- A. J. Papa, , J. Appl. Polym. Sci, 16, pp.2361~ (1972)
- N. Grassie, , Eur. Polym. J, 16, pp.113~ (1980)
- N. Grassie, , Polym. Degrad. Stab, 5, pp.89~ (1983)
- T. C. Chang, , Polym. Degrad. Stab, 49, pp.353~ (1995)
- T. Wolf, , J. Am. Chem. Soc, 139, pp.11064~11072 (2017)
- M.-S. Yen, , J. Appl. Polym. Sci, 67, pp.1301~ (1998)
- S. V. Levchik, , Polym. Int, 53 (2004)