첨가제 및 소결조건에 따른 무급유 베어링 강판 기공성 평가
An Evaluation on Apparent Porosity of Plates according to the Filler and Sintering Conditions for Oilless Bearing
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Recently, the interest in the development of Oilless bearings, which is a kind of sliding bearing, has been attracting to industry. Oilless bearings are mainly used in areas where fluid lubrication is difficult to apply because of large contact area. The purpose of this study is to develop products with higher load and durability compared to the conventional oilless bearing. For this purpose, the optimal steel sheet was obtained and the porosity evaluation was carried out by evaluating bronze sinterability for various steel sheets. The conclusion obtained is as follows.; It was found that steel plate suitable for bronze powder plate is SPCC CR (Cold Rolled). The average porosity of KAG-23, KAG-23G and PBF-8 specimens was 16.8%, 17.8% and 22.1%, respectively, indicating that the porosity of PBF-8 specimen was the highest. As the number of rolling increases, the surface porosity decreases rapidly.
Abstract
Recently, the interest in the development of Oilless bearings, which is a kind of sliding bearing, has been attracting to industry. Oilless bearings are mainly used in areas where fluid lubrication is difficult to apply because of large contact area. The purpose of this study is to develop products with higher load and durability compared to the conventional oilless bearing. For this purpose, the optimal steel sheet was obtained and the porosity evaluation was carried out by evaluating bronze sinterability for various steel sheets. The conclusion obtained is as follows.; It was found that steel plate suitable for bronze powder plate is SPCC CR (Cold Rolled). The average porosity of KAG-23, KAG-23G and PBF-8 specimens was 16.8%, 17.8% and 22.1%, respectively, indicating that the porosity of PBF-8 specimen was the highest. As the number of rolling increases, the surface porosity decreases rapidly.
참고문헌 (11)
- 김홍근, "금형 베어링 개수에 따른 A-IMS 튜블러 샤프트의 가공 진직도 개선", 한국기계기술학회지, 19(3), pp.396~401 (2017), 한국기계기술학회[DOI]
- 조상경, "볼 베어링의 마멸 상태에 따른 진동 특성의 변화", 한국트라이볼로지학회지, 33(4), pp.141~147 (2017), 한국트라이볼로지학회[DOI]
- 이동현, "터빈 시뮬레이터용 틸팅패드 저널베어링의 열윤활 해석 및 패드 온도 측정", 한국트라이볼로지학회지, 33(3), pp.112~118 (2017), 한국트라이볼로지학회[DOI]
- 박민혁, "유한요소해석을 이용한 오일리스 베어링의 분말 압축 성형에 관한 시뮬레이션", 한국기계가공학회지, 12(2), pp.1~7 (2013), 한국기계가공학회
- H. S. Kong, "Friction and Wear at Dry Sliding Low Carbon Steel Surfaces Under Vacuum Conditions", Journal of KSTLE, 10(3), pp.29~38 (1994)
- C. W. Kim, "A Study on Manufacturing and Characteristics of Solid Lubricant Oilless Bearing", Korean Journal of Materials Research, 11(11), pp.99~996 (2001)
- H. D. Yang, "Evaluation on Performance of Sintered Oilless Bearing with Cu-coated Ferrous Powder as alternative of Bronze Powder", International Symposium on Advanced Powder Metallurgy (2003)
- H. S. Kong, "An Evaluation Analysis on the Maximum Allowable PV Value of Oilless Composite Bearing Materials", Journal of KSTLE, 11(1), pp.27~36 (1995)
- M. F. Ashby, "Temperature maps for frictional heating in dry sliding", STLE Tribology Trans., 34(4), pp.577~587 (1991)[DOI]
- S. I. Byun, "A Study of the PTFE Coating on Metal Bearing" (1987)
- 권일현, "무급유 베어링 최적 소결조건 도출을 위한 첨가제에 따른 겉보기 기공률 특성 평가", 한국기계기술학회지, 19(5), pp.759~763 (2017), 한국기계기술학회[DOI]