Al6061-T6의 SP시험에 의한 FSW 용접부 파괴특성 연구
The Evaluation of Fracture Characteristics of Friction Stir Welded Al6061-T6 with Small Punch Test
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
In this study, Equivalent fracture strain and Fracture energy were evaluated with the small punch test(SP test) for friction stir welded(FSW) Al6061-T6 sheets. With the three rotation speeds and the three feeding rate, The nine different conditions of FSW were prepared for the SP test. The SP test specimens were manufacturedand tested on the advancing side, center, and retreating side to the tool rotation direction. From the SP test data, the equivalent fracture strain and the fracture energy were analyzed. The high value of equivalent fracture strain was attained form tool rotational speed 900RPM and feeding rate 330mm/min. It is found that its characteristic is about 14% higher than the value of condition 1100RPM-330mm/min that have the lowest value. The high value of fracture energy was obtained from the tool rotation speed 900RPM and feeding rate 330mm/min. The lowest fracture energy, which from 1000RPM-300mm/min, was approximately 16% difference to the highest value.
Abstract
In this study, Equivalent fracture strain and Fracture energy were evaluated with the small punch test(SP test) for friction stir welded(FSW) Al6061-T6 sheets. With the three rotation speeds and the three feeding rate, The nine different conditions of FSW were prepared for the SP test. The SP test specimens were manufacturedand tested on the advancing side, center, and retreating side to the tool rotation direction. From the SP test data, the equivalent fracture strain and the fracture energy were analyzed. The high value of equivalent fracture strain was attained form tool rotational speed 900RPM and feeding rate 330mm/min. It is found that its characteristic is about 14% higher than the value of condition 1100RPM-330mm/min that have the lowest value. The high value of fracture energy was obtained from the tool rotation speed 900RPM and feeding rate 330mm/min. The lowest fracture energy, which from 1000RPM-300mm/min, was approximately 16% difference to the highest value.
참고문헌 (14)
- 이광진, "마찰교반용접(FSW) 및 마찰교반처리(FSP)의 최신 연구개발 동향", 대한용접접합학회지, 31(2), pp.26~29 (2013), 대한용접접합학회
- 방한서, "스테인리스강의 마찰교반접합 기술 개발 동향", 대한용접접합학회지, 30(5), pp.407~409 (2012), 대한용접접합학회
- 정용하, "마찰교반처리법을 이용한 복합재료 제조의 최근 동향", 대한용접접합학회지, 30(5), pp.410~415 (2012), 대한용접접합학회
- 천창근, "타이타늄 소재 마찰교반용접 기술 동향", 대한용접접합학회지, 31(2), pp.16~20 (2013), 대한용접접합학회
- 김영곤, "알루미늄 다이캐스팅 합금의 마찰교반접합특성", 한국기계기술학회지, 16(3), pp.1463~1467 (2014), 한국기계기술학회[DOI]
- 김영곤, "곡면 마찰교반접합에 따른 Al 5083의 맞대기 접합부기계적 특성에 대한 연구", 한국기계기술학회지, 18(5), pp.674~679 (2016), 한국기계기술학회[DOI]
- H. S. Yu, "A study on stress corrosion cracking susceptibility evaluation of welded steel joint by Small Punch Test", pp.1994
- D. M. Rodrigues, "High speed friction stir welding of aluminium alloys", Science and Technology of Welding and Joining, 15(8), pp.678~681 (2010)
- H. J. Liu, "Effect of welding speed on microstructure and mechanical properties of self-reacting friction stir welded 6061-T6 aluminum alloy", Materials & Design, 50, pp.872~878 (2013)[DOI]
- 선신규, "기계구조용 탄소강 중공축의 마찰 용접후 열처리의 기계적 특성", 한국기계기술학회지, 19(4), pp.561~566 (2017), 한국기계기술학회[DOI]
- Y. J. Lee, "Establishment of optimal friction stir weldment condition for Al6061-T6 by Small punch test", pp.2012
- 김범준, "몽크만 · 그랜트관계에 기초한 소형펀치 크리프시험 데이터와 일축 크리프시험 데이터의 관계", 한국정밀공학회지, 30(8), pp.809~814 (2013), 한국정밀공학회
- X. Mao, "Characterization of Fracture Behavior in Small Punch Test by Combined Recrystallization-Etch Method and Rigid Plastic Analysis", Journal of Testing & Evaluation, 15(1), pp.30~37 (1987)[DOI]
- S. J. Sun, "Evaluation of Mechanical Properties of AZ61 Magnesium Alloy Joints at various Welding Speeds"