Technical Investigation into the In-situ Electron Backscatter Diffraction Analysis for the Recrystallization Study on Extra Low Carbon Steels: Regular Article
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Technical investigation to figure out the problems arising during in-situ heating electron backscatter diffraction (EBSD) analysis inside scanning electron microscopy (SEM) was carried out. EBSD patterns were successfully acquired up to 830oC without degradation of EBSD pattern quality in steels. Several technical problems such as image drift and surface microstructure pinning were taking place during in-situ experiments. Image drift problem was successfully prevented in constant current supplying mode. It was revealed that the surface pinning problem was resulted from the TiO2 oxide particle formation during heating inside SEM chamber. Surface pinning phenomenon was fairly reduced by additional platinum and carbon multi-layer coating before in-situ heating experiment,furthermore was perfectly prevented by improvement of vacuum level of SEM chamber via leakage control. Plane view in-situ observation provides better understanding on the overall feature of recrystallization phenomena and cross sectional in-situ observation provides clearer understanding on the recrystallization mechanism.
Abstract
Technical investigation to figure out the problems arising during in-situ heating electron backscatter diffraction (EBSD) analysis inside scanning electron microscopy (SEM) was carried out. EBSD patterns were successfully acquired up to 830oC without degradation of EBSD pattern quality in steels. Several technical problems such as image drift and surface microstructure pinning were taking place during in-situ experiments. Image drift problem was successfully prevented in constant current supplying mode. It was revealed that the surface pinning problem was resulted from the TiO2 oxide particle formation during heating inside SEM chamber. Surface pinning phenomenon was fairly reduced by additional platinum and carbon multi-layer coating before in-situ heating experiment,furthermore was perfectly prevented by improvement of vacuum level of SEM chamber via leakage control. Plane view in-situ observation provides better understanding on the overall feature of recrystallization phenomena and cross sectional in-situ observation provides clearer understanding on the recrystallization mechanism.
참고문헌 (23)
- <112> textures in cold rolled and annealed IF sheet steel, "ISIJ Int", 1999, 923~929
- Choi S H, "Primary recrystallization modelling for interstitial free steels", Mater. Sci. Eng. A, 405, pp.86~101 (2005)
- Emren F, "Investigation of the development of the recrystallization textures in deep drawing steels by ODF analysis", Acta Metall, 34, pp.2105~2117 (1986)
- Hansen N, "Recrystallization kinetics in copper investigated by in situ texture measurements by neutron diffraction", Acta Metall, 29, pp.1523~1533 (1981)
- Hashimoto N, "Texture evolution of IF steel due to recrystallization", ISIJ Int, 38, pp.617~624 (1998)
- Hurley P J, "A study of recrystallization in singlephase aluminium using in-situ annealing in the scanning electron microscope", J. Microsc, 213, pp.225~234 (2004)
- Hutchinson W B, "Development and control of annealing textures in low-carbon steels", Int. Mater. Rev, 29, pp.25~42 (1984)
- Kim D I, "Statistical analysis of the development of recrystallization texture in IF steel", Mater. Sci. Forum, pp.408~844 (2002)
- Mirpuri K, "Texture evolution in Copper film at high temperature studied in situ by electron back-scatter diffraction", Thin Solid Films, 496, pp.703~717 (2006)
- Nakamichi H, "In-Situ EBSD Observation of the Recrystallization of an IF Steel at High Temperature", Mater. Sci. Forum, 550, pp.441~446 (2007)
- Nakamichi H, "Recrystallization phenomena in an IF steel observed by in situ EBSD experiments", J. Microsc, 230, pp.464~471 (2008)
- Quadir M Z, "Deformation banding and recrystallization of α fibre components in heavily rolled IF steel", Acta Mater, 52, pp.4011~4021 (2004)
- Quadir M Z, "A microstructural study of the origins of γ recrystallization textures in 75% warm rolled IF steel", Acta Mater, 54, pp.4337~4350 (2006)
- Randle V, "Introduction to Texture Analysis: Macrotexture, Microtexture and Orientation Mapping" (2000), Gordon and Breach Science Publishers
- Ray R K, "Cold rolling and annealing textures in low carbon and extra low carbon steels", Int. Mater. Rev, 39, pp.129~172 (1994)
- Samajdar I, "Physical parameters related to the developments of recrystallization textures in an ultra low carbon steel", Acta Mater, 47, pp.55~65 (1998)
- Samajdar I, "Development of recrystallization texture in IF-steel: an effort to explain developments in global texture from microtextural studies", Acta Mater, 46, pp.2751~ (1998)
- Seaton N C A, "Nucleation during recrystallisation in Ti-SULC steel", Mater. Sci. Forum, pp.467~470 (2004)
- Sharma P K, "Mean square amplitude of thermal vibrations in cubic metals at melting point", Chem. Phys. Lett, 4, pp.1~2 (1969)
- Takechi H, "Metallurgical aspects on interstitial free sheet steel from industrial viewpoints", ISIJ Int, 34, pp.1~8 (1994)
- Thomas I, "High-resolution EBSD investigation of deformed and partially recrystallized IF steel", Adv. Eng. Mater, 5, pp.566~570 (2003)
- Tse Y Y, "Orientation imaging microscopy studies of recrystallization in interstitial-free steel", Metall. Mater. Trans, 37, pp.1055~1064 (2006)
- Wright S I, "Electron Backscatter Diffraction in Materials Science", pp.329~344 (2009), Springer