고로슬래그시멘트를 사용한 다공성 황토콘크리트의 성능 평가
Performance Evaluation of Porous Hwang-toh Concrete Using Blast Furnace Slag Cement
2
조회
0
다운로드
10
인용
0
참고문헌
초록
This study aims to evaluate a porous concrete using hwang-toh, blast furnace slag and blast furnace slag (BFS) cement instead of type I cement. The tests that were carried out to analysis the properties of porous hwang-toh BFS cement concrete included compressive strength, continuous void ratio, absorption rate, and pH value, repeated freezing and thawing test were conducted. Test results indicated that the performance in porous hwang-toh concrete are effective on the kaoline based binder materials. The pH value were shown in about 9.5 ~ 8.5. The compressive strength was increased and void ratio was decreased with increasing the kaoline based binder materials, respectively. The void ratio and compressive strength were in the range of about 21 ~ 30 %, 8 ~ 13 MPa, respectively. The increased in void ratio of more than 25 % is showed to reduce the resistance of repeated freezing and thawing. Also, the resistance of repeated freezing of thawing and the compressive strength of porous hwang-toh BFS cement concrete are independent with hwang-toh content and BFS cement amount. But, the void ratio was decreased with increasing the high volume hwang-toh contents (more than 15 %).
Abstract
This study aims to evaluate a porous concrete using hwang-toh, blast furnace slag and blast furnace slag (BFS) cement instead of type I cement. The tests that were carried out to analysis the properties of porous hwang-toh BFS cement concrete included compressive strength, continuous void ratio, absorption rate, and pH value, repeated freezing and thawing test were conducted. Test results indicated that the performance in porous hwang-toh concrete are effective on the kaoline based binder materials. The pH value were shown in about 9.5 ~ 8.5. The compressive strength was increased and void ratio was decreased with increasing the kaoline based binder materials, respectively. The void ratio and compressive strength were in the range of about 21 ~ 30 %, 8 ~ 13 MPa, respectively. The increased in void ratio of more than 25 % is showed to reduce the resistance of repeated freezing and thawing. Also, the resistance of repeated freezing of thawing and the compressive strength of porous hwang-toh BFS cement concrete are independent with hwang-toh content and BFS cement amount. But, the void ratio was decreased with increasing the high volume hwang-toh contents (more than 15 %).
참고문헌 (15)
- Choi, H. Y., "Experimental Study on the Properties of Concrete by the Kinds of Admixture and the Replacement Ratios of Activated Hwangtoh", Journal of the korea concrete institute, 13(2), pp.123~129 (2001)
- Choi, L., "Eco-Concrete", Magazine of the korea concrete institute, 10(6), pp.11~21 (1998)
- 강성수, "황토결합재를 이용한 콘크리트의 수화열과 수축특성", 콘크리트학회 논문집, 20(5), pp.549~555 (2008), 한국콘크리트학회
- A Study on Developing Porous Concrete using non-firing binder, "Nature and Environment Inc", Ecosystem Engineering Research Center, ~ (2002)
- Manufacturing Process of Porous Concrete Using Blast Furnace Slag, Hwangtoh, Recycling Aggregates, Report of construction new technology, 2006, "Nature and Environment Inc", ~ (2006)
- 박승범, "산업부산물을 이용한 포러스콘크리트의 식생능력평가", 콘크리트학회 논문집, 14(4), pp.623~629 (2002), 한국콘크리트학회
- Park, S. B., "Concrete for Planting", Magazine of the korea concrete institute, 12(5), pp.38~42 (2000)
- 성찬용, "식생을 위한 다공성 콘크리트의 중성화 처리 및 양생방법에 따른 pH 저감에 관한 실험적 연구", 한국농공학회논문집, 44(2), pp.99~106 (2002), 한국농공학회
- 성찬용, "볏짚재를 활용한 식생콘크리트 블록 개발 및 사면 적용성에 관한 실험적 연구", 한국농공학회논문집, 45(4), pp.107~114 (2003), 한국농공학회
- Shim, K. Y., "Effects of Sodding and Seeding Time and Rate of Seed Mixture on the Establishment of Cool-Season Turfgrasses", Journal of the Korean Turfgrass Society, 18(4), pp.179~191 (2004)
- 윤준노, "폐활성탄을 사용한 다공성 콘크리트의 물리․역학적 성질", 한국농공학회논문집, 51(4), pp.21~27 (2009), 한국농공학회
- 성찬용, "볏짚재를 혼입한 다공성콘크리트 블록의 식생을 위한 공학적 특성", 콘크리트학회 논문집, 16(3), pp.311~318 (2004), 한국콘크리트학회
- 양근혁, "혼화제？재가 무시멘트 황토 모르터의 유동성 및 압축강도 발현에 미치는 영향", 콘크리트학회 논문집, 18(6), pp.793~800 (2006), 한국콘크리트학회
- 원종필, "혼합 시멘트 모르타르의 내구특성", 한국농공학회논문집, 45(3), pp.41~49 (2003), 한국농공학회
- 원종필, "고반응성 메타카올린을 사용한 고성능 콘크리트의 특성", 콘크리트학회 논문집, 14(3), pp.349~356 (2002), 한국콘크리트학회