Corrosion Characteristics of Welding Zones by Laser and TIG Welding of 304 Stainless Steel
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Two types of welding methods were performed on austenitic 304 stainless steel: laser welding and TIG welding. The differences of the corrosion characteristics of the welded zones from the two welding methods were investigated with electrochemical methods, such as measurement of the corrosion potential, polarization curves, cyclic voltammogram, etc. The vickers hardness of all laser-welded zones (WM:Weld Metal, HAZ:Heat Affected Zone, BM:Base Metal) was relatively higher while their corrosion current densities exhibited a comparatively lower value than those which were TIG welded. In particular, the corrosion current density of the TIG-welded HAZ had the highest value among all other welding zones, which suggests that chromium depletion due to the formation of chromium carbide occurs in the HAZ, which is in the sensitization temperature range, thus it can easily be corroded with an active anode. Intergrenular corrosion was also observed at the TIG-welded HAZ and WM zones. Consequently, we can see that corrosion resistance of all austenitic 304 stainless steel welding zones can be improved via the use of laser welding.
Abstract
Two types of welding methods were performed on austenitic 304 stainless steel: laser welding and TIG welding. The differences of the corrosion characteristics of the welded zones from the two welding methods were investigated with electrochemical methods, such as measurement of the corrosion potential, polarization curves, cyclic voltammogram, etc. The vickers hardness of all laser-welded zones (WM:Weld Metal, HAZ:Heat Affected Zone, BM:Base Metal) was relatively higher while their corrosion current densities exhibited a comparatively lower value than those which were TIG welded. In particular, the corrosion current density of the TIG-welded HAZ had the highest value among all other welding zones, which suggests that chromium depletion due to the formation of chromium carbide occurs in the HAZ, which is in the sensitization temperature range, thus it can easily be corroded with an active anode. Intergrenular corrosion was also observed at the TIG-welded HAZ and WM zones. Consequently, we can see that corrosion resistance of all austenitic 304 stainless steel welding zones can be improved via the use of laser welding.
참고문헌 (11)
- P. D. Bilmes, , Corro. Sci., 48, pp.3270~ (2006)
- V. S. Raja, , Corro. Sci., 40, pp.1609~ (1998)
- L. W. Tsay, , Corro. Sci, 39, pp.1165~ (1997)
- T. M. Devine, , Corro. Sci., 30, pp.135~ (1990)
- F. Nubu, , J. Jap. Weld. Soc., 33, pp.55~ (1964)
- M.Yoshihiko, , J. Jap. Weld. Soc., 41, pp.154~ (1972)
- 김영훈, "The Effect of Welding Method on the Electrochemical Behavior of Austenitic Stainless Steel Sheet", CORROSION SCIENCE AND TECHNOLOGY, 9(3), pp.122~128 (2010), 한국부식방식학회
- 김진경, "선박용 디젤기관의 주철부품 보수용접 특성에 관한 연구", 한국해양공학회지, 20(2), pp.41~45 (2006), 한국해양공학회
- D. H. Joon, "Control of Corrosion and Anti-corrosion", pp.294~ (1985), Il Jung Sa Publishing
- Geon-Sang Roh, "Evaporation Heat Transfer Characteristics of Hydrocarbon Refrigerants R-290 and R-600a in the Horizontal Tubes", 한국마린엔지니어링학회지, 31(1), pp.74~83 (2007), 한국마린엔지니어링학회
- J. V. Muylder, "Atlas of Electrochemical Equilibria in Aqueous Solution, Pourbaix, Rergomon press and cebelcor", 260~509 (1966)