Inherent Damage Zone Model for Fatigue Strength Evaluation of Cracks and Notches
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Abstract
Inherent damage zone model is presented to explain the fatigue properties near the fatigue limit and the crack growth threshold consistently. Inherent damage zone model assumes that the stress at a point which is located at a small distance, , an inherent length of the material that represents the size of effective damage zone, from the crack initiation position governs the fatigue characteristics regardless of the geometric configuration of the specimen; smooth specimen, notched specimen or cracked specimens with short and long crack length. A special feature of the paper is using the exact stress distributions of notched and cracked specimens at the strength evaluations. Analytical elastic solutions by Neuber and Westergaard are employed for this purpose. Relationship between fatigue limit of smooth specimen and threshold stress of cracked specimen, occurrence condition of non-propagating crack at the root of elliptic notch and circular hole and relationship between stress concentration factor and fatigue notch factor are discussed quantitatively based on the proposed model.
참고문헌 (14)
- "강재의 해수환경중에서의 피로강도평가에 관한 연구" (1997)
- "CO2용접이음재의 대기 및 해수중에서의 회전굽힘 피로강도에 관한 연구", 37(2), pp.118~126 (2000)
- "선박의 표면조도에 관한 연구 추정법 및 선박성능에 미치는 영향", 33(2), pp.31~35 (1996)
- "부식효과를 고려한 선체구조 검사계획안의 최적화", 36(4), pp.137~146 (1999)
- "유조선 종강도부재의 확률론적 부식속도 예측모델의 개발", 35(2), pp.83~93 (1998)
- "Corrosion Fatigue Test Method for the Material", pp.34~43
- "Influence of Cl-Concentration on Corrosion Fatigue Crack Growth of an Austenitic Stainless Steel Transactions of the Japan Society of Mechanical Engineers", 48, pp.1489~1495 (1982)
- "A Study on the Fatigue Strength of Rusting Decayed Steel Plates", (93), pp.97~102 (1997)
- "Corrosion Fatigue Crack Growth in High Tensile Strength Steel under Cathodic Overprotection", mi 33(shima), pp.1407~1413 (1984)
- "Studies on the Evaluation of Corrosion Fatigue Crack Initiation Journal of The Society of Naval Architects of Japan", 142, pp.239~250 (1977)
- "Influence of Notch Sensitivity on Fatigue Strength of Steel Sheets Corroded with Salt-Water", 20, pp.1375~1380 (1987)
- "On Corrosion Fatigue Strength of High Tensile Steels", 28, pp.887~893 (1979)
- "A Study on the Corrosion Fatigue Strength of Ballast Tank", pp.411~417 (1996), Shipbuilding Research Association of Japan
- "Fatgiue Strength of Corroded Weld Joints", 176, pp.481~489