Effect to optical properties by changing the Al2O3 ratio in K2O-Al2O3-P2O5 glasses
2
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
In this study, we prepared glasses with the composition of 0.1% Ce-doped (100−x) KPO3-xAl2O3 and investigated luminescent characteristics. The glass samples with different Al2O3 ratio (x = 5, 10, 15, 20, 25, 30 and 40) were synthesized by the melt quenching method. The All samples had high transmittance (80−90%) at wavelengths longer than 350 nm except for x = 40, and by increasing the Al2O3 ratio, the transmittance of the samples was improved. From the measurements of photoluminescence (PL) decay curve, the luminescence decay time was confirmed to be typical for the 5d−4f transition of Ce3+ (~30 ns). The samples showed thermally-stimulated luminescence (TSL), and the sensitivity of dose response was confirmed to be linear in the dose range from 0.01 mGy to 1 Gy for the x = 25 and 30 samples which showed the highest sensitivity among the present samples. The scintillation spectra show the broad luminescence around 300−500 nm, and these emission intensities were increased by increasing the Al2O3 ratio.
Abstract
In this study, we prepared glasses with the composition of 0.1% Ce-doped (100−x) KPO3-xAl2O3 and investigated luminescent characteristics. The glass samples with different Al2O3 ratio (x = 5, 10, 15, 20, 25, 30 and 40) were synthesized by the melt quenching method. The All samples had high transmittance (80−90%) at wavelengths longer than 350 nm except for x = 40, and by increasing the Al2O3 ratio, the transmittance of the samples was improved. From the measurements of photoluminescence (PL) decay curve, the luminescence decay time was confirmed to be typical for the 5d−4f transition of Ce3+ (~30 ns). The samples showed thermally-stimulated luminescence (TSL), and the sensitivity of dose response was confirmed to be linear in the dose range from 0.01 mGy to 1 Gy for the x = 25 and 30 samples which showed the highest sensitivity among the present samples. The scintillation spectra show the broad luminescence around 300−500 nm, and these emission intensities were increased by increasing the Al2O3 ratio.
참고문헌 (24)
- T. Yanagida, , IEEE Trans. Nucl. Sci, 57, pp.1492~1495 (2010)
- D. Totsuka, , Nucl. Instruments Methods Phys. Res. Sect. A Accel. Spectrometers, Detect. Assoc. Equip, 659, pp.399~402 (2011)
- S. Moriuchi, , Japanese J. Heal. Phys, 44, pp.122~133 (2009)
- Y. Miyamoto, , Radiat. Meas, 55, pp.72~74 (2013)
- T. Yanagida, , Jpn. J. Appl. Phys, 52, pp.076401~ (2013)
- T. Itoh, , IEEE Trans. Nucl. Sci, 53, pp.2983~2990 (2006)
- K. Yamaoka, , IEEE Trans. Nucl. Sci, 52, pp.2765~2772 (2005)
- T. Yanagida, , Opt. Mater, 35, pp.1987~1992 (2013)
- S. W. S. McKeever, , Radiat. Meas, 46, pp.1336~1341 (2011)
- Takayuki Yanagida, , Proceedings of the Japan Academy, Series B, 94, pp.75~97 (2018)
- Y. Miyamoto, , Radiat. Meas, 45, pp.546~549 (2010)
- A. B. Corradi, , J. Mater. Sci, 41, pp.2811~2819 (2006)
- S. Tanabe, , Am. Phys. Soc, 45, pp.4620~4625 (1992)
- T. Kuro, , Opt. Mater, 62, pp.561~568 (2016)
- H. Tatsumi, , J. Ceram. Soc. Japan, 124, pp.550~553 (2016)
- D. Shiratori, , J. Mater. Sci. Mater. Electron
- A. Moguš-Milanković, , J. Non. Cryst. Solids, 289, pp.204~213 (2001)
- S. Kaur, , 143, pp.31~37 (2013)
- R. Reisfeld, , Spectrochim. Acta Part A Mol. Biomol. Spectrosc, 54, pp.2143~2150 (1998)
- T. Yanagida, , J. Ceram. Soc. Japan, 121, pp.988~991 (2013)
- T. Yanagida, , Opt. Mater, 35, pp.2480~2485 (2013)
- "International Glass Database System INTERGLAD Ver. 7 released", New Glass Forum
- Y. Isokawa, , J. Non. Cryst. Solids, 487, pp.1~6 (2018)
- "CHIYODA TECHNOL Corp."[URL]