Microstructure and mechanical properties of yttrium aluminum garnet porous ceramics prepared by different sintering process parameters
0
조회
0
다운로드
6
인용
0
참고문헌
키워드
초록
Yttrium aluminum garnet (YAG), which possesses excellent properties, is investigated and applied. The sintering technology of YAG porous ceramics is optimized. Results show that the porosity initially increases and then decreases with an increase of increasing temperature rate, the porosity are decreased with an increase of removing carbon temperature, the porosity are decreased with an increase of sintering temperature, the porosity are decreased with an increase of holding time. Meanwhile, the compressive strength constantly exhibits an opposite tendency. The optimization of the sintering technology of YAG porous ceramics is based on porosity and compressive strength. A good sintering technology are an increasing temperature rate of 8 oC/min, a removing carbon temperature of 800 oC, removing carbon time of 1 h, a sintering temperature of 1450 oC and holding time of 2 h. The porosity of the prepared YAG porous ceramics is 57.4%, and the compressive strength is 8.89 MPa.
Abstract
Yttrium aluminum garnet (YAG), which possesses excellent properties, is investigated and applied. The sintering technology of YAG porous ceramics is optimized. Results show that the porosity initially increases and then decreases with an increase of increasing temperature rate, the porosity are decreased with an increase of removing carbon temperature, the porosity are decreased with an increase of sintering temperature, the porosity are decreased with an increase of holding time. Meanwhile, the compressive strength constantly exhibits an opposite tendency. The optimization of the sintering technology of YAG porous ceramics is based on porosity and compressive strength. A good sintering technology are an increasing temperature rate of 8 oC/min, a removing carbon temperature of 800 oC, removing carbon time of 1 h, a sintering temperature of 1450 oC and holding time of 2 h. The porosity of the prepared YAG porous ceramics is 57.4%, and the compressive strength is 8.89 MPa.
참고문헌 (20)
- Z. Feng, , J. Porous Mater, 25, pp.189~198 (2018)
- H. Wang, , Sci. Adv, 3, pp.1~9 (2017)
- N. Arai, , Script. Mater, 162, pp.72~76 (2019)
- B. Zhang, , J. Eur. Ceram. Soc, 39, pp.1775~1780 (2019)
- B. Ren, , Ceram. Int, 45, pp.6581~6584 (2019)
- P. Q. Zhao, , J. Alloy. Compd, 748, pp.36~43 (2018)
- T. D. Afolabi, , Int. J. Appl. Ceram. Tech, 15, pp.1060~1071 (2018)
- S. Stub, , J. Mater. Chem. A, 6, pp.8265~8270 (2018)
- S. Baitalik, , J. Mater. Sci, 53, pp.6350~6365 (2018)
- Jieguang Song, "The effect of the sintering temperature on the properties of porous YAG ceramics", Journal of Ceramic Processing Research, 19(1), pp.11~14 (2018), 청정에너지연구소[DOI]
- J. Kraxner, , Mater. Letts, 204, pp.181~183 (2017)
- G. H. Zhou, , Int. J. Adv. Manuf. Tech, 95, pp.1677~1684 (2018)
- Jie-Guang Song, "Infuluence of sintering technology on microstructure and mechanical properties of YAG", ZrB2 ceramics, 2013, pp.14(3), 376~379[DOI]
- J. Hostasa, , J. Eur. Ceram. Soc, 39, pp.53~58 (2019)
- X. Wang, , J. Am. Ceram. Soc, 100, pp.1~7 (2017)
- N. Adilah A. Hassan, , Mater. Today, 7, pp.601~606 (2019)
- C. Settgast, , J. Eur. Ceram. Soc, 39, pp.610~617 (2019)
- N. Chawake, , Script. Mater, 161, pp.36~39 (2019)
- H. Shao, , Mater. Sci. Eng. A, 724, pp.231~238 (2018)
- Z. J. Yu, , J. Adv. Ceram, 8, pp.112~120 (2019)