Contact wear of Low-Zirconia Toughened Alumina (ZTA) produced by a colloidal process
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
This study focuses on the wear and related mechanical properties of zirconia-toughened alumina (ZTA) composites with 4.7- 30 vol% yttria doped-TZP (YTZP) particulates. A colloidal process was used to achieve a homogeneous distribution of fine TZP grains in an alumina matrix. Mechanical properties, flexural strength, hardness, fracture toughness, and contact wear were measured. Quantified microstructures by SEM are also reported. A wear-resistant ZTA with a low-zirconia content (< 5%) was obtained by improvements in microstructural homogeneity and optimization.
Abstract
This study focuses on the wear and related mechanical properties of zirconia-toughened alumina (ZTA) composites with 4.7- 30 vol% yttria doped-TZP (YTZP) particulates. A colloidal process was used to achieve a homogeneous distribution of fine TZP grains in an alumina matrix. Mechanical properties, flexural strength, hardness, fracture toughness, and contact wear were measured. Quantified microstructures by SEM are also reported. A wear-resistant ZTA with a low-zirconia content (< 5%) was obtained by improvements in microstructural homogeneity and optimization.
참고문헌 (8)
- B.L. Karihaloo, , J. Am. Ceram. Soc, 74(7), pp.1703~1706 (1991)
- P.F. Becher, , J. Am. Ceram. Soc, 76(3), pp.657~663 (1993)
- D.J. Kim, , J. BiomadicalMat. Res, 54(4), pp.438~443 (2000)
- T. Xu, J, , J. Europ. Ceram. Soc, 26(7), pp.1205~1211 (2006)
- 3Y-TZP, MS thesis, "Study on Processing and Mechanical Propertiesof Al2O3", pp.2006, M.T. Weng
- CNS standard, "Method of test for flexural strengthof high performance ceramics", Wear, pp.162~164 (1993)
- A.H. Heuer, , J.Am. Ceram. Soc, 65(12), pp.642~650 (1982)
- C. S. Hwang, "Ceramic Technology Handbook", pp.699~ (1999)