Electrode properties of porous La2NiO4+δ layers screen-printed on a Ce0.8Sm0.2O2-δ electrolyte
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
A La2NiO4+δ/Ce0.8Sm0.2O2-δ/La2NiO4+δ symmetrical cell was prepared using a screen-printing method by sintering at 1100℃. The electrochemical properties of the cell were examined by the impedance spectroscopy technique under zero dc bias in air between 500-700℃. The La2NiO4+δ electrodes displayed satisfactory chemical and thermodynamic compatibilities with the Ce0.8Sm0.2O2-δ electrolyte. A comparatively low area specific resistance of 0.18 Ω cm2 at 700℃ was determined for the La2NiO4+δ electrodes. Scanning electron microscope (SEM) observation revealed that the La2NiO4+δ electrodes showed a reasonable porosity, a well-necked connection among fine grains and a tight adhesion to the electrolyte support. The desired microstructure is regarded to be responsible for the superior electrode properties of the La2NiO4+δ layers.
Abstract
A La2NiO4+δ/Ce0.8Sm0.2O2-δ/La2NiO4+δ symmetrical cell was prepared using a screen-printing method by sintering at 1100℃. The electrochemical properties of the cell were examined by the impedance spectroscopy technique under zero dc bias in air between 500-700℃. The La2NiO4+δ electrodes displayed satisfactory chemical and thermodynamic compatibilities with the Ce0.8Sm0.2O2-δ electrolyte. A comparatively low area specific resistance of 0.18 Ω cm2 at 700℃ was determined for the La2NiO4+δ electrodes. Scanning electron microscope (SEM) observation revealed that the La2NiO4+δ electrodes showed a reasonable porosity, a well-necked connection among fine grains and a tight adhesion to the electrolyte support. The desired microstructure is regarded to be responsible for the superior electrode properties of the La2NiO4+δ layers.
참고문헌 (28)
- Y. Teraoka, , Mater. Res. Bull., 23, pp.51~58 (1988)
- S.J. Beson, , J. Electrochem. Soc., 146, pp.1305~1309 (1999)
- L.W. Tai, , Solid State Ionics, 76, pp.259~271 (1995)
- L.W. Tai, , Solid State Ionics, 76, pp.273~283 (1995)
- A. Petric, , Solid State Ionics, 135, pp.719~725 (2000)
- N. Dasgupta, , Mater. Sci. Eng., B90, pp.278~286 (2002)
- Q. Xu, , J. Alloy. Compd., 429, pp.34~39 (2007)
- V. Dusastre, , Solid State Ionics, 126, pp.163~174 (1999)
- Q. Xu, , J. Alloy. Compd., 454, pp.460~465 (2008)
- V.V. Vashook, , Solid State Ionics, 110, pp.245~253 (1998)
- V.V. Vashook, , Solid State Ionics, 119, pp.23~30 (1999)
- V.V. Kharton, , J. Mater. Chem., 9, pp.2623~2639 (1999)
- S.J. Skiner, , Solid State Ionics, 135, pp.709~712 (2000)
- J.A. Kilne, , Solid State Ionics, 154, pp.523~527 (2002)
- E. Boehm, , Solid State Sci., 5, pp.973~981 (2003)
- T. Tsai, , Solid State Ionics, 98, pp.191~196 (1997)
- J.M. Bassat, , Fifth European Solid Oxide Fuel Cell Forum Proceedings, European Fuel Cell Forum, pp.586~593 (2002)
- F. Mauvy, , J. Euro. Ceram. Soc., 25, pp.2669~2672 (2005)
- G. Amow, , Solid State Ionics, 177, pp.1205~1210 (2006)
- F. Mauvy, , J. Electrochem. Soc., 158, pp.A1547~A1553 (2006)
- M.J. Escudero, , J. Electroanal. Chem., 611, pp.107~116 (2007)
- D. Perez-Coll, , J. Power Sources, 178, pp.151~162 (2008)
- E.P. Murray, , Solid State Ionics, 143, pp.265~273 (2001)
- D.P. Huang, , J. Zhou, Mater. Lett.,, 60, pp.1892~1895 (2006)
- M. Chen, , Ceram. Int, 35, pp.1335~1343 (2009)
- D.P. Huang, , Ceram. Int., 34, pp.651~655 (2008)
- S.B. Adler, , J. Electrochem. Soc., 143, pp.3554~3564 (1996)
- N.T. Hart, , J. Power Sources, 106, pp.42~50 (2002)