Preparation and characterization of a silicon oxycarbide coating with crack-healing capability for silicon carbide ceramics
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
Silicon carbide ceramics have good mechanical and thermal properties, but they have a failure problem by brittle fracture due to fast crack growth. Attempts were made to self-heal cracks in ceramics. The SiC ceramics were coated with silicon oxycarbide glass films which were prepared by dip-coating and pyrolysis of polymer precursors. The crack-healing capability was evaluated by mechanical testing and microstructural analysis. Cracks were artificially generated in the sample by either micro indentation or notch making. Healing treatments at 1100, 1300, 1400, or 1500 oC were made. Bending strengths were measured before and after crack growth and a healing treatment. It was found that the strength dropped low by the generation of cracks but was fully recovered after the healing treatment. The cracks were found filled and healed by the coating material.
Abstract
Silicon carbide ceramics have good mechanical and thermal properties, but they have a failure problem by brittle fracture due to fast crack growth. Attempts were made to self-heal cracks in ceramics. The SiC ceramics were coated with silicon oxycarbide glass films which were prepared by dip-coating and pyrolysis of polymer precursors. The crack-healing capability was evaluated by mechanical testing and microstructural analysis. Cracks were artificially generated in the sample by either micro indentation or notch making. Healing treatments at 1100, 1300, 1400, or 1500 oC were made. Bending strengths were measured before and after crack growth and a healing treatment. It was found that the strength dropped low by the generation of cracks but was fully recovered after the healing treatment. The cracks were found filled and healed by the coating material.
참고문헌 (14)
- A.W. Weimer, "Carbide, Nitride, and Boride Materials Synthesis and Processing" (1997), Chapman and Hall
- T. Ekstrom, , J.Mater.Sci.Lett, 8(9), pp.1067~1070 (1989)
- B.S. Kim, , J.Kor.Cer.Soc, 30(12), pp.999~1006 (1993)
- K. W. Nam, , J. Kor. Soc. Mech. Engineering, 47(1), pp.67~71 (2007)
- 남기우, "고강도 사이알론의 균열치유와 고온강도 특성", 대한기계학회논문집 A, 33(09), pp.957~962 (2009), 대한기계학회
- 남기우, "Si₃N₄ 세라믹스의 균열 치유와 굽힘 강도 특성", 대한기계학회논문집 A, 32(11), pp.957~962 (2008), 대한기계학회
- 남기우, "Y2O3 첨가량에 의한 Al2O3 복합재 세라믹스의 균열 균열 치유와 고온 굽힘강도 특성", 대한기계학회논문집 A, 31(11), pp.1108~1114 (2007), 대한기계학회
- K. Ando, , J.Kor.Soc.Power Sys.Eng, 6(1), pp.88~95 (2002)
- Jondo Yun, "Crack-healing capability and high temperature oxidation resistance of multilayer coatings for carbon-carbon composites", Journal of Ceramic Processing Research, 10(3), pp.340~343 (2009), 세라믹공정연구센터
- T. Rouxel, , J.Sol-Gel Sci.Technol, 14, pp.87~94 (1999)
- C. G. Pantano, , J.Sol-Gel Sci.Technol, 14, pp.7~25 (1999)
- G. M. Renlund, , J.Mater.Res, 6(12), pp.2716~2722 (1991)
- "Korean Industrial Standards L1591", Korean Agency for Technology and Standards, ~ (2008)
- R. Hertzberg, "Deformation and fracture mechanics of engineering materials" (1989), John Wiley & Sons