Comparative studies on mechanical properties and cutting performance of Cr-Al-Si-N coated micro tool for high speed machining applications were performed. Quaternary Cr-Al-Si-N coatings, in which Si was incorporated into Cr-Al-N, were synthesized onto WC-Co substrates using a hybrid system of an arc ion plating (AIP) and DC magnetron sputtering techniques. The high hardness of Cr-Al-Si-N coatings was related to the composite microstructure consisting of fine CrN crystallites and amorphous Si3N4. The hardness values of the Cr-Al-Si-N (~55 GPa) coatings were significantly increased compared with those of Cr-Al-N (~24 GPa) coatings. Cutting tests were carried out to evaluate the performances of micro endmill coated tool in high-speed cutting conditions. Consequently, the quaternary Cr-Al-Si (8.7 at.%)-N coated micro end-mill under dry machining showed good cutting performance in micro end-milling process of AISI D2 work material (HRC 24).
Abstract
Comparative studies on mechanical properties and cutting performance of Cr-Al-Si-N coated micro tool for high speed machining applications were performed. Quaternary Cr-Al-Si-N coatings, in which Si was incorporated into Cr-Al-N, were synthesized onto WC-Co substrates using a hybrid system of an arc ion plating (AIP) and DC magnetron sputtering techniques. The high hardness of Cr-Al-Si-N coatings was related to the composite microstructure consisting of fine CrN crystallites and amorphous Si3N4. The hardness values of the Cr-Al-Si-N (~55 GPa) coatings were significantly increased compared with those of Cr-Al-N (~24 GPa) coatings. Cutting tests were carried out to evaluate the performances of micro endmill coated tool in high-speed cutting conditions. Consequently, the quaternary Cr-Al-Si (8.7 at.%)-N coated micro end-mill under dry machining showed good cutting performance in micro end-milling process of AISI D2 work material (HRC 24).
참고문헌 (16)
- H. Scheerer, , Surf. Coat. Technol, 200, pp.203~207 (2005)
- 김진호, "A layer-by-layer self-assembly method for organic-inorganic hybrid multilayer thin films", Journal of Ceramic Processing Research, 10(6), pp.770~773 (2009), 세라믹공정연구센터
- Y. K. Jeong, , Curr Appl. Phys, 9, pp.141~144 (2009)
- J. Lin, , J. Nanosci. Nanotechnol, 9, pp.3514~3523 (2009)
- S. Q. Wang, , Int. J. of Refractory Met. & Hard Mater, 28, pp.593~596 (2010)
- C. L. Chang, , Thin Solid Films, 519, pp.4923~4927 (2011)
- T. Miyake, , Surf. Coat. Technol, 205, pp.290~294 (2010)
- C. Kim, , Curr Appl. Phys, 9, pp.145~148 (2009)
- D. Mercs, , Surf. Coat. Technol, 200, pp.403~ (2005)
- M. C. Kang, , Surf. Coat. Technol, 200, pp.1939~1944 (2005)
- I. W. Park, , J. Vac. Sci. Technol, 21, pp.895~ (2003)
- S. Carvalho, , Thin Solid Films, 391, pp.398~399 (2001)
- I. W. Park, , J. Vac. Sci. Technol, 21, pp.895~ (2003)
- Kwang Soo Choi, "Synthesis by a PECVD technique and mechanical properties of nc-Ti(B,N)", a-BN coatings, 2011, pp.12(2), 160~164[DOI]
- D. Rafaja, , Surf. Coat. Technol, 201, pp.9476~9484 (2007)
- S. Veprek, , Appl. Phys. Lett, 66, pp.2640~ (1995)