PTCR characteristics of porous Y-doped (Ba,Sr)TiO3 ceramics prepared using nano-size carbon black as a pore precursor
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Carbon black (0 to 60 vol%) was added to (Ba,Sr)TiO3 powder. The resulting mixture was treated by sonication and freeze drying. The effects of the carbon black content on the microstructure and PTCR characteristics of the resulting porous (Ba,Sr)TiO3 ceramics were investigated. The combined process of sonication and freeze drying was an effective method for preparing a homogeneous dispersion of nano-size carbon black. The porosities of all (Ba,Sr)TiO3 ceramics were < 10%. The PTCR jump of the (Ba,Sr)TiO3 ceramics prepared with carbon black was > 106 , and increased slightly with increasing carbon black content. Carbon black is an effective additive for BaTiO3-based ceramics, showing excellent PTCR characteristics. The change in the resistivity of porous (Ba,Sr)TiO3 ceramics can be explained in terms of the change in potential barrier height due to the chemisorption/desorption of oxygen atoms at the grain boundaries.
Abstract
Carbon black (0 to 60 vol%) was added to (Ba,Sr)TiO3 powder. The resulting mixture was treated by sonication and freeze drying. The effects of the carbon black content on the microstructure and PTCR characteristics of the resulting porous (Ba,Sr)TiO3 ceramics were investigated. The combined process of sonication and freeze drying was an effective method for preparing a homogeneous dispersion of nano-size carbon black. The porosities of all (Ba,Sr)TiO3 ceramics were < 10%. The PTCR jump of the (Ba,Sr)TiO3 ceramics prepared with carbon black was > 106 , and increased slightly with increasing carbon black content. Carbon black is an effective additive for BaTiO3-based ceramics, showing excellent PTCR characteristics. The change in the resistivity of porous (Ba,Sr)TiO3 ceramics can be explained in terms of the change in potential barrier height due to the chemisorption/desorption of oxygen atoms at the grain boundaries.
참고문헌 (19)
- B. Huybrechts, , J. Mater. Sci. Rev, 30, pp.2463~2474 (1995)
- H. Emoto, , J. Ceram. Soc. Jpn, 100, pp.555~559 (1992)
- H. F. Cheng, , J. Am. Ceram. Soc, 76, pp.827~832 (1993)
- I. C. Ho, , J. Am. Ceram. Soc, 76, pp.2385~2388 (1993)
- I. C. Ho, , J. Am. Ceram. Soc, 77, pp.829~832 (1994)
- B. C. Lacourse, , J. Am. Ceram. Soc, 78, pp.3352~3356 (1995)
- M. Kuwabara, , J. Am. Ceram. Soc, 64, pp.639~644 (1981)
- M. Kuwabara, , J. Am. Ceram. Soc, 64, pp.C170~C171 (1981)
- T. Takahashi, , J. Ceram. Soc. Jpn, 98, pp.879~884 (1990)
- T. R. Shrout, , J. Mater. Sci, 26, pp.145~154 (1991)
- S. M. Su, , J. Am. Ceram. Soc, 77, pp.2154~2156 (1994)
- J. G. Kim, , Mater. Sci. Eng. B, 77, pp.255~260 (2000)
- 이기주, "카본블랙을 첨가하여 제조한 다공성 BaTiO_3계 세라믹스의 미세구조 및 PTCR 특성 변화", 한국분말야금학회지, 18(1), pp.41~48 (2011), 한국분말야금학회
- Q. Cheng, , J. Phys. Chem. C, 114, pp.8821~8827 (2010)
- T. Fukasawa, , J. Am. Ceram. Soc, 85, pp.2151~2155 (2002)
- J. Lee, , J. Control. Release, 111, pp.185~192 (2006)
- S.A. Saltykov, "Stereometric Metallography" (1958), Metallurgizdat
- K. Park, , Mat. Sci. Eng. B, 107, pp.19~26 (2004)
- J. B. Nelson, , Proc. Phys. Soc, 57, pp.160~177 (1945)