Effect of reducing agent on the crystallization characteristics and properties of Baiyunebo east mine tailing glass-ceramics
2
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
Ingredient manipulations of raw materials were always an important issue in the field of recycling silicate solid wastes of mining and metallurgy processes. For this purpose, glass-ceramics of CaO-MgO-Al2O3-SiO2 quaternary system were successfully produced by the method of melting, using Baiyunebo east mine tailing and fly ash as main sources of raw materials. The effect of carbon powder variation on the crystallization, and properties of the glass-ceramics were systematically investigated by differential thermal analysis (DTA), X-ray diffraction (XRD), Raman microscopy, scanning electron microscope (SEM) and mechanical testing. The results showed though carbon powder addition cannot change the formation of main crystal phase (augite), the concentration of this primary crystalline phase can be enhanced with the increase of the carbon powder addition to 5.6 wt%. As a result, the density, bending strength, acid-resistance and activation energy of the materials can be manipulated accordingly. And the mechanism of our manipulating process was close related to the reduction effect of carbon powder on decreasing the valence and concentration of iron ion within the studied glass ceramics.
Abstract
Ingredient manipulations of raw materials were always an important issue in the field of recycling silicate solid wastes of mining and metallurgy processes. For this purpose, glass-ceramics of CaO-MgO-Al2O3-SiO2 quaternary system were successfully produced by the method of melting, using Baiyunebo east mine tailing and fly ash as main sources of raw materials. The effect of carbon powder variation on the crystallization, and properties of the glass-ceramics were systematically investigated by differential thermal analysis (DTA), X-ray diffraction (XRD), Raman microscopy, scanning electron microscope (SEM) and mechanical testing. The results showed though carbon powder addition cannot change the formation of main crystal phase (augite), the concentration of this primary crystalline phase can be enhanced with the increase of the carbon powder addition to 5.6 wt%. As a result, the density, bending strength, acid-resistance and activation energy of the materials can be manipulated accordingly. And the mechanism of our manipulating process was close related to the reduction effect of carbon powder on decreasing the valence and concentration of iron ion within the studied glass ceramics.
참고문헌 (17)
- Y. Zhao, , Ceram. Int, 38, pp.2495~2500 (2012)
- A. Sukran Demirkiran, "Senol Yilmaz and Ugur Sen", J.Ceram.Process.Res, 102-103, pp.112~115 (2012)
- D. H. Vu, , Waste Manage, 32, pp.2306~2314 (2012)
- G. A. Khater, , J. Non-Cryst. Solids, 358, pp.1128~1134 (2012)
- K. Sharma, , J. Non-Cryst. Solids, 358, pp.1886~1891 (2012)
- P. Alizadeh, , J. Eur. Ceram. Soc, 24, pp.3529~3533 (2004)
- S. M. Wang, , J. Alloys Compd, 509, pp.2819~2823 (2011)
- A. Karamanov, , J. Non-Cryst. Solids, 281, pp.139~151 (2001)
- T. Zhao, , Mater. Sci. Eng. B, 170, pp.22~25 (2010)
- S. M. Wang, , Phase Transit, 83, pp.397~403 (2010)
- A. Karamanov, , J. Am. Ceram. Soc, 83, pp.3153~3157 (2000)
- B. W. Li, , Trans. Indian Ceram. Soc, 72, pp.119~123 (2013)
- Z. H. Yang, , J. Alloys Compd, 574, pp.354~360 (2013)
- C. J. Liu, , J. Iron Steel Res. Int, 14, pp.73~78 (2007)
- P. M. Sørensen, , J. Non-Cryst. Solids, 351, pp.1246~1253 (2005)
- N. Lonnroth, , J. Non-Cryst. Solids, 354, pp.1190~1193 (2008)
- E. Huang, , Am. Mineral, 85, pp.473~479 (2000)