Experimental study on self-healing effect of FRCC with PVA fibers and additives
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
It has been confirmed that some types of fiber-reinforced cementitious composites (FRCCs), particularly the ones that use synthetic fibers (e.g. polyvinyl alcohol; PVA), have a great capability to self-heal the cracks by some previous research. In this study, self-healing capability of FRCCs with additives such as silica fume and excess PVA dosage was tested. Two experimental studies were carried out to evaluate the self-healing capability with different levels of cracks. As to Test I, freeze/ thaw cycles (according to the JIS A 1148 (ASTM C 666-A) method) was subjected to specimens to introduce micro cracks. As to Test II, visible cracks up to 500 µm width were generated by tensile loading test. The damaged FRCC specimens were exposed to several conditions to induce self-healing curing. In the case of Test I (freeze/thaw cycles), the self-healing capability was evaluated by measuring the number of cracks, relative dynamic Young’s-modulus (RDYM) and pore structures. In the case of Test II (tensile loading test), the coefficient of watertightness was measured every certain period of time. Upon exposing to the curing conditions after the damage, the results showed a recovery by means of self-healing effect. In Test I, all of the cracks and RDYM recovered due to the densification of microstructures and filling up of the cracks. In Test II, the recovery of the coefficient of watertightness was confirmed after self-healing curing, which was proportionally consistent during the immersion in water. Moreover, the results showed that an admixture of PVA could be expected to enhance the selfhealing capability of cracks without causing any negative impact on the properties of FRCC.
Abstract
It has been confirmed that some types of fiber-reinforced cementitious composites (FRCCs), particularly the ones that use synthetic fibers (e.g. polyvinyl alcohol; PVA), have a great capability to self-heal the cracks by some previous research. In this study, self-healing capability of FRCCs with additives such as silica fume and excess PVA dosage was tested. Two experimental studies were carried out to evaluate the self-healing capability with different levels of cracks. As to Test I, freeze/ thaw cycles (according to the JIS A 1148 (ASTM C 666-A) method) was subjected to specimens to introduce micro cracks. As to Test II, visible cracks up to 500 µm width were generated by tensile loading test. The damaged FRCC specimens were exposed to several conditions to induce self-healing curing. In the case of Test I (freeze/thaw cycles), the self-healing capability was evaluated by measuring the number of cracks, relative dynamic Young’s-modulus (RDYM) and pore structures. In the case of Test II (tensile loading test), the coefficient of watertightness was measured every certain period of time. Upon exposing to the curing conditions after the damage, the results showed a recovery by means of self-healing effect. In Test I, all of the cracks and RDYM recovered due to the densification of microstructures and filling up of the cracks. In Test II, the recovery of the coefficient of watertightness was confirmed after self-healing curing, which was proportionally consistent during the immersion in water. Moreover, the results showed that an admixture of PVA could be expected to enhance the selfhealing capability of cracks without causing any negative impact on the properties of FRCC.
참고문헌 (12)
- H. Mihashi, "Development of Engineered Self-Healing and Self-Repairing Concrete-State-of-the-Art Report", Journal of Advanced Concrete Technology, 10(5), pp.170~184 (2012)
- M. De Rooij, "Self-Healing Phenomena in Cement-Based Materials-State-of-the-Art Report of RILEM Thechnical Committee 221-SHC: Self-Healing Phenomena in Cement-Based Materials" (2013), Springer
- S. Igarashi, "Research activity of JCI technical committee TC-075B: Autogenous healing in cementitious materials", pp.89~96
- E. Herbert, "Self-Healing of Microcracks in Engineered Cementitious Composites (ECC) Under a Natural Environment", Materials, 6(7), pp.2831~2845 (2013)
- H. M. Jonkers, "Self Healing Materials. An Alternative Approach to 20 Centuries of Material Science", pp.195~204 (2007), Springer
- T. Nishiwaki, "Development of Self-Healing System for Concrete with Selective Heating around Crack", Journal of Advanced Concrete Technology, 4(2), pp.267~275 (2006)
- C. Joseph, "Experimental investigation of adhesive-based self-healing of cementitious materials", Magazine of Concrete Research, 62(11), pp.831~843 (2010)
- D. Homma, "Self-Healing Capability of Fibre Reinforced Cementitious Composites", Journal of Advanced Concrete Technology, 7(2), pp.217~228 (2009)
- T. Nishiwaki, "Experimental Study on Self-Healing Capability of FRCC Using Different Types of Synthetic Fibers", Journal of Advanced Concrete Technology, 10(6), pp.195~206 (2012)
- T. Matsumura, "Properties of frost damaged concrete and the estimation of the degree of frost damage", Journal of Structural and Construction Engineering (Transactions of AIJ), 563, pp.9~13 (2003)
- Y. Kishimoto, "The Effect of Vertical Distribution of Water Permeability on the Modeled Neutralization Process in Concrete Walls", Journal of ASTM International, 4(1), pp.JAI100323~ (2007)
- C. Edvardsen, "Water permeability and autogenous healing of cracks in concrete", ACI Materials Journal, 96, pp.448~454 (1999)