Effect of AlN content on the properties and microstructure of pressureless-sintered Al2O3-AlN composites
2
조회
0
다운로드
4
인용
0
참고문헌
키워드
초록
Aluminium oxide (Al2O3)-aluminium nitride (AlN) composites were prepared at 1500-1600 oC by pressureless sintering. Themain raw materials used were AlN and Al2O3, and appropriate amounts of TiO2-Y2O3-CaO-La2O3 quaternary sintering aidswere added. The effects of different AlN contents and sintering temperatures on the bulk density, bending strength, Rockwellhardness, thermal conductivity, and other properties of Al2O3-based ceramics were studied. The phase composition andmicrostructure of the samples were analysed with an X-ray diffractometer and scanning electron microscope. Results showedthat the Al2O3-AlN composites had excellent overall performance in terms of a flexural strength of 295.7MPa, a Rockwellhardness of 61.5 HRA, and a thermal conductivity of 38.8W/(m·K) (at 25 oC) after pressureless sintering at 1600 oC for 3 hwith 10 wt% AlN content. These properties met the requirements of high-power ceramic LED lamp holders. The Al2O3-10 wt%AlN composites sintered at 1600 oC had a dense microstructure, tight bonding among grains, and few pores, whichexplained the excellent performance of the samples.
Abstract
Aluminium oxide (Al2O3)-aluminium nitride (AlN) composites were prepared at 1500-1600 oC by pressureless sintering. Themain raw materials used were AlN and Al2O3, and appropriate amounts of TiO2-Y2O3-CaO-La2O3 quaternary sintering aidswere added. The effects of different AlN contents and sintering temperatures on the bulk density, bending strength, Rockwellhardness, thermal conductivity, and other properties of Al2O3-based ceramics were studied. The phase composition andmicrostructure of the samples were analysed with an X-ray diffractometer and scanning electron microscope. Results showedthat the Al2O3-AlN composites had excellent overall performance in terms of a flexural strength of 295.7MPa, a Rockwellhardness of 61.5 HRA, and a thermal conductivity of 38.8W/(m·K) (at 25 oC) after pressureless sintering at 1600 oC for 3 hwith 10 wt% AlN content. These properties met the requirements of high-power ceramic LED lamp holders. The Al2O3-10 wt%AlN composites sintered at 1600 oC had a dense microstructure, tight bonding among grains, and few pores, whichexplained the excellent performance of the samples.
참고문헌 (19)
- G. Shi, , J. Alloy. Compd., 628, pp.413~415 (2015)[DOI]
- N.C. Fan, "Porous Al2O3 catalyst carrier by 3D additive manufacturing for syngas reforming", Journal of Ceramic Processing Research, 18(9), pp.676~682 (2017), 청정에너지연구소[DOI]
- H.S. Kim, , Ceram. Int., 36, pp.2039~2045 (2010)[DOI]
- C. Liu, , J. Am. Ceram. Soc., 100, pp.3380~3384 (2017)[DOI]
- L.A.F. Junior, , Ceram. Int., 42, pp.18718~18723 (2016)[DOI]
- X. Chen, , J. Chin. Ceram. Soc., 39, pp.495~501 (2011)
- X. Chen, , J. Synthetic Cryst. Soc., 39, pp.1422~1428 (2010)
- F.C. Sahin, , J. Eur. Ceram. Soc., 32, pp.925~929 (2012)[DOI]
- X.B. Li, , J. Eur. Ceram. Soc., 35, pp.2027~2032 (2015)[DOI]
- Q.G. Li, , J. Alloy. Compd., 636, pp.20~23 (2015)[DOI]
- F. Boey, , Acta Mater., 49, pp.3117~3127 (2001)[DOI]
- A. Maghsoudipour, , J. Eur. Ceram. Soc., 25, pp.1067~1072 (2005)[DOI]
- A. Maghsoudipour, , Ceram. Int., 30, pp.773~783 (2004)[DOI]
- Y.W. Kim, , Ceram. Int., 34, pp.1849~1855 (2008)[DOI]
- J.F. Ravidge, , J. Mater. Sci., 3, pp.629~638 (1968)[DOI]
- 이화준, "Effect of Additive Size on the Densification and Thermal Conductivity of AlN Ceramics with MgO–CaO–Al2O3–SiO2 Additives", 한국세라믹학회지, 54(1), pp.43~48 (2017), 한국세라믹학회
- T. Nishimura, , Adv. Appl. Ceram., 113, pp.89~93 (2014)[DOI]
- L.F. Huang, "Low temperature sintering of alumina ceramics using simple slurry casting method", pp.2007
- Z.P. Xie, "Structural ceramics" (2011), Tsinghua University Press