Effect of CeO2 addition on crystallization and thermophysical properties of Li2O-ZnO-SiO2 glass-ceramics
2
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
The effect of CeO2 addition on crystallization and thermo-physical properties of lithium zinc silicate (LZS) glasses containingLi2O-ZnO-SiO2-Al2O3-Na2O-P2O5 was investigated. The changes of CeO2 contents (2-8 wt.%) had an obvious influence on thetransition temperatures (Tg) and crystallization temperatures (Tc) of LZS glass-ceramics, and they increased with CeO2 contentincreasing. According to XRD analysis, CeO2 promoted the formation of cristobalite and β-spodumene crystals, and β-spodumene increased obviously. As the CeO2 content increasing, the microstructure and microhardness (being 6.88 Gpa at 880oC) of glass-ceramics had great changes. The average thermal expansion coefficient (20 - 450 oC) showed first increasing thendecreasing, having a wide range. The maximum of thermal expansion coefficient was obtained when the glass-ceramicscontained 4 wt.% CeO2, being 175×10−7 K−1 (at 700 oC) and 178×10−7 K−1 (at 880 oC) respectively. Excellent thermo-physicalproperties indicate the glass has greater potential application, such as being used as sealing glass.
Abstract
The effect of CeO2 addition on crystallization and thermo-physical properties of lithium zinc silicate (LZS) glasses containingLi2O-ZnO-SiO2-Al2O3-Na2O-P2O5 was investigated. The changes of CeO2 contents (2-8 wt.%) had an obvious influence on thetransition temperatures (Tg) and crystallization temperatures (Tc) of LZS glass-ceramics, and they increased with CeO2 contentincreasing. According to XRD analysis, CeO2 promoted the formation of cristobalite and β-spodumene crystals, and β-spodumene increased obviously. As the CeO2 content increasing, the microstructure and microhardness (being 6.88 Gpa at 880oC) of glass-ceramics had great changes. The average thermal expansion coefficient (20 - 450 oC) showed first increasing thendecreasing, having a wide range. The maximum of thermal expansion coefficient was obtained when the glass-ceramicscontained 4 wt.% CeO2, being 175×10−7 K−1 (at 700 oC) and 178×10−7 K−1 (at 880 oC) respectively. Excellent thermo-physicalproperties indicate the glass has greater potential application, such as being used as sealing glass.
참고문헌 (34)
- S. C. Clausbruch, , J. Non-Cryst. Solids, 263, pp.388~394 (2000)
- B. I. Shaima, , J. Mater. Lett, 58, pp.2423~2438 (2004)
- I.W. Donald, , J. Non-cryst. solids, pp.345~346 (2004)
- M. Goswami, , J. Phys. Chem. Solid, 71, pp.739~744 (2010)
- W. Z. Liu, , Thermochim. Acta, 584, pp.45~50 (2014)
- Y. Z. Chen, , Ceram. Int, 42, pp.11650~11653 (2016)
- S. M. Salman, , Bol. Soc. Esp. Ceram. V, 56, pp.205~214 (2017)
- P. W. McMillan, , Glass Tech, 7, pp.121~ (1966)
- P. W. McMillan, , Glass Tech, 7, pp.128~ (1966)
- I. W. Donald, , J. Mater. Sci, 24, pp.3892~3903 (1989)
- I. W. Donald, , J. Mater. Sci, 46, pp.1975~2000 (2011)
- A. Karamanov, , J. Eur. Ceram. Soc, 20, pp.2233~2237 (2000)
- J. J. Shyu, , J. Am. Ceram. Soc, 83, pp.635~639 (2000)
- A. W. A El-Shennawi, , Ceram. Int, 27, pp.725~730 (2001)
- W. Zheng, , Thermochim. Acta, 456, pp.69~74 (2007)
- H. B. Zhang, , Chinese J. Inorg. Chem, 26, pp.144~148 (2010)
- Yasemin Demirci, "Crystallization behavior and properties of cordierite glassceramics with added boron oxide", Journal of Ceramic Processing Research, 12(3), pp.352~356 (2011), 청정에너지연구소[DOI]
- Z. Shen, , Ceram. Int, 43, pp.7099~7105 (2017)
- 이다영, "Thermal properties of glass-ceramics made with zircon and diopside powders", Journal of Ceramic Processing Research, 19(6), pp.504~508 (2018), 청정에너지연구소[DOI]
- G. P. Singh, , Physica B, 406, pp.640~644 (2011)
- E. Mansour, , J. Non-Cryst. Solids, 357, pp.1364~1369 (2011)
- P. S. Gurinder, , Physica B, 407, pp.4168~4172 (2012)
- H. J. Wang, , Int. J. Appl. Glass Sci, 7, pp.310~318 (2016)
- H. J. Wang, , J. Mater Sci-Mater. El, 27, pp.2860~2865 (2016)
- T. Liu, , Ceram. Int, 39, pp.5553~5559 (2013)
- F. Soleimani, , Mater. Res. Bull, 47, pp.1362~1367 (2012)
- S. A. M. Abdel-Hameed, , J. Alloys Compd, 554, pp.371~377 (2013)
- S. B. Sohn, , J. Mater. Sci, 35, pp.4815~4821 (2000)
- A. M. Hu, , Ceram. Int, 31, pp.11~14 (2005)
- Jadambaa Temuujin, "Influence of cerium oxide (CeO2) addition on the mechanical properties of glass ceramics precursor prepared from fly ash", Journal of Ceramic Processing Research, 18(2), pp.112~115 (2017), 청정에너지연구소[DOI]
- Du Yongsheng, "Effect of aggregates of elements induced by rare earth doping on toughening of tailing-derived glass-ceramics", Journal of Ceramic Processing Research, 20(4), pp.401~410 (2019), 청정에너지연구소[DOI]
- M. Goswami, , Ceram. Int, 33, pp.863~867 (2007)
- A. X. Lu, , J. Non-cryst. Solids, 353, pp.2692~2697 (2007)
- J. Zarzycki, "Material Science and Technology", pp.667~713 (1991), Weinheim press