Effects of ZrO2 on the properties and dry-pressing preparation of mullite based crossing network structure
1
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
Mullite based crossing network structure were dry-pressing prepared by using waste gangue and calmogastrin as the main rawmaterial. Effects of ZrO2 on the properties of the samples were studied. The samples were characterized by X-ray diffraction,scanning electron microscopy and the corresponding energy dispersive analysis. The experiment results showed that whenZrO2 content was 20%, the sample reached 123.21 MPa of bending strength, 123.75% of bending strength retention rate andthe coefficient of thermal expansion of 5.023×106/oC-1. It could be attributed to the crossing network structure of the mullite,which produced a lot of pore porosity to accommodate a certain expansion deformation and thus alleviate the heat stress. Moreover, micro cracks around the porosity can be formed in the main crack tip region, which decreases local elastic strainenergy and restrains the crack propagation and thus enhances the materials properties.
Abstract
Mullite based crossing network structure were dry-pressing prepared by using waste gangue and calmogastrin as the main rawmaterial. Effects of ZrO2 on the properties of the samples were studied. The samples were characterized by X-ray diffraction,scanning electron microscopy and the corresponding energy dispersive analysis. The experiment results showed that whenZrO2 content was 20%, the sample reached 123.21 MPa of bending strength, 123.75% of bending strength retention rate andthe coefficient of thermal expansion of 5.023×106/oC-1. It could be attributed to the crossing network structure of the mullite,which produced a lot of pore porosity to accommodate a certain expansion deformation and thus alleviate the heat stress. Moreover, micro cracks around the porosity can be formed in the main crack tip region, which decreases local elastic strainenergy and restrains the crack propagation and thus enhances the materials properties.
참고문헌 (18)
- M. Zhao, , J. Gra. Natur. Sci. Med, 33, pp.17~19 (2012)
- D. Xu, , Chn. Steel, 5, pp.11~15 (2011)
- H. Schneider, , J. Eur. Ceram. Soc, 28(2), pp.329~344 (2008)
- K. Cui, , Coatings, 10(7), pp.672~ (2020)
- C. Sadik, , J. As. Ceram. Soc, 2(2), pp.83~96 (2014)
- M. Hamidouche, , J. Eur. Ceram. Soc, 16(4), pp.441~445 (1996)
- J. Guo, , J. CHN. Ceram. Soc, 1, pp.7~17 (1996)
- X. Gu, , Key. Eng. Mater., 602-603, pp.628~631 (2014)
- G. Li, "Phase basement and refactory material diagrams", pp.1~ (1994), Metallurgical Industry Press
- W. Dong, , J. Ceram. Soc. Jpn, 125(2), pp.75~78 (2017)
- N. M. Rendtorff, , Ceram. Int, 34(8), pp.2017~2024 (2008)
- N. M. Rendtorff, , Ceram. Int, 35(2), pp.779~786 (2009)
- A. Gungor, , Ceram. Int, 38(5), pp.4189~4194 (2012)
- T. M. Souza, , Ceram. Int, 40(1), pp.1699~1707 (2014)
- N.M. Rendtorff, , Mat. Sci. Eng. A, 498(1-2), pp.208~215 (2008)
- S. Xia, , Refract, 4, pp.192~194 (1998)
- G. T. M. Stam, , Int. J. Sol. Struct, 31(14), pp.1923~1948 (1994)
- I. Yu. Prokhorov, , Refract. Ind. Ceram, 39(5), pp.189~197 (1998)