Hydrochloric Acid Leaching Behavior of Mechanically Activated Black Dross
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Effect of ball milling treatment on the hydrochloric acid leaching performance of black dross was investigated to recover alumina. Ball milling time and speed showed limited effect on the leaching behavior of the alumina in the mechanically dross. Under the optimum mechanical activation condition (for 1h at 700 rpm), the leaching of alumina in hydrochloric acid solution was significantly affected by leaching time and reaction temperature. MgO was completely dissolved in most of the leaching conditions, while a small amount of Ca, Fe, Si and Ti oxides was dissolved. Although 80% of alumina was dissolved, the dissolved minor components such as Ca, Fe, Mg, Si and Ti oxides should be separated to recover pure alumina solution.
Abstract
Effect of ball milling treatment on the hydrochloric acid leaching performance of black dross was investigated to recover alumina. Ball milling time and speed showed limited effect on the leaching behavior of the alumina in the mechanically dross. Under the optimum mechanical activation condition (for 1h at 700 rpm), the leaching of alumina in hydrochloric acid solution was significantly affected by leaching time and reaction temperature. MgO was completely dissolved in most of the leaching conditions, while a small amount of Ca, Fe, Si and Ti oxides was dissolved. Although 80% of alumina was dissolved, the dissolved minor components such as Ca, Fe, Mg, Si and Ti oxides should be separated to recover pure alumina solution.
참고문헌 (25)
- Sarker, M. S. R., "Extraction and characterization of alumina nanopowders from aluminum dross by acid dissolution process", Int. J. Miner. Metall. Mater., 22, pp.429~436 (2015)[DOI]
- Tsakiridis, P. E., "Aluminium recovery during black dross hydrothermal treatment", J. Environ. Chem. Eng., 1, pp.23~32 (2013)[DOI]
- David, E., "Hydrolysis of aluminum dross material to achieve zero hazardous waste", J. Hazard. Mater., 209-210, pp.501~509 (2016)
- Meshram, A., "Recovery of valuable products from hazardous aluminum dross: A review", Resour. Conserv. Recycl., 130, pp.95~108 (2018)[DOI]
- Bruckard, W. J., "Characterisation and treatment of Australian salt cakes by aqueous leaching", Miner. Eng., 20, pp.1376~1390 (2007)[DOI]
- Dash, B., "Acid dissolution of alumina from waste aluminium dross", Hydrometallurgy, 92, pp.48~53 (2008)[DOI]
- Nguyen, T. T. N., "Ball milling treatment of black dross for selective dissolution of alumina in sodium hydroxide leaching", Processes, 6(4), pp.1~11 (2018)[DOI]
- Valeev, D., "Extraction of aluminium by autoclave hydrochloric acid leaching of boehmite-kaolinite bauxite", TMS Light Met., pp.23~28 (2016)
- Boukerche, I., "Degradability of aluminum in acidic and alkaline solutionsm", Corros. Sci., 78, pp.343~352 (2014)[DOI]
- Thi Thuy Nhi Nguyen, "Leaching of Black Dross by Hydrochloric Acid Solutions", 자원리싸이클링, 26(6), pp.58~64 (2017), 한국자원리싸이클링학회[DOI]
- 행위동, "Treatment of Black Dross with Water and NaOH Solution", 자원리싸이클링, 26(3), pp.53~60 (2017), 한국자원리싸이클링학회[DOI]
- Han, Q., "Characterisation and milling time optimisation of nanocrystalline aluminium powder for selective laser melting", Int. J. Adv. Manuf. Technol., 88, pp.1429~1438 (2017)[DOI]
- Tokoro, C., "Silicate removal in aluminum hydroxide co-precipitation process", Materials (Basel), 7, pp.1084~1096 (2014)[DOI]
- Willey, J. D., "Reactions which remove dissolved alumina from seawater", Mar. Chem., 3, pp.227~240 (1975)[DOI]
- Chemical interactions of aluminum with aqueous silica at 25 degrees Celsius, Geol. Surv. Water-Supply Pap., 1827-E, "Hem, J. D.", ~ (1973)
- Yokoyama, T., "A study of the alumina-silica gel adsorbent for the removal of silicic acid from geothermal water: Increase in adsorption capacity of the adsorbent due to formation of amorphous aluminosilicate by adsorption of silicic acid", J. Colloid Interface Sci., 252, pp.1~5 (2002)[DOI]
- Maraghechi, H., "Effect of calcium on dissolution and precipitation reactions of amorphous silica at high alkalinity", Cem. Concr. Res., 87, pp.1~13 (2016)[DOI]
- Hill, J., "The effect of sodium chloride on the dissolution of calcium silicate hydrate gels", Waste Manag., 26, pp.758~768 (2006)[DOI]
- Teir, S., "Dissolution of natural serpentinite in mineral and organic acids", Int. J. Miner. Process., 83, pp.36~46 (2007)[DOI]
- Rodriguez, A., "Amorphous Iron Silicate Scales in Surface Pipelines: Characterization and Geochemical Constraints on Formation Conditions in the Miravalles Geothermal Field" (2006)
- Xiong, X., "Preparation of <TEX>$TiO_2$<", TEX> from ilmenite using sulfuric acid decomposition of the titania residue combined with separation of <TEX>$Fe^{3+}$<, Adv. Powder Technol., pp.2013, 24[DOI]
- Arabia, S., "Extraction of Alumina from Local Clays by Hydrochloric Acid Process", JKAU Eng. Sci., 20, pp.29~41 (2009)
- Gorrepati, E. A., "Silica precipitation in acidic solutions: Mechanism, pH effect, and salt effect", Langmuir, 26, pp.10467~10474 (2010)[DOI]
- Xiao, J., "Separation of aluminum and silica from coal gangue by elevated temperature acid leaching for the preparation of alumina and SiC", Hydrometallurgy, 155, pp.118~124 (2015)[DOI]
- Sheikholeslami, R., "Silica Fouling - effect of Ca, Mg, and Pretreatment by Sodium Aluminate, and Softeners", 6th World Congr. Chem. Eng., pp.23~27 (2015)