국내산 흑연의 구형화에 미치는 로터 속도의 영향

Abstract

The circularity and particle size distribution of products obtained from dry classification after circularity tests using a high-intensity mixer were investigated to evaluate the use of domestic graphite concentrate as a lithium-ion battery material. At a rotor sp eed of 3 ,000 rpm, the p article size and c ircularity o f the concentrated sample and p roduct were unchanged. The circularity increased and particle size decreased when the rotor speeds were increased to 6,000 rpm, 10,000 rpm, and 12,000 rpm and the operating time was increased. For instance, the circularity increased from 0.870 to 0.936 when the rotor speed was increased from 3,000 rpm to 12,000 rpm for an operating time of 10 min. After the circularity test, dry classification was performed, wherein the circularity of the coarse particles was found to have increased to 0.947. Round particles were observed in the SEM images, indicating that high circularity was successfully achieved.