가압·가열 처리한 층층나무 적층재를 활용한 테이블 디자인 연구
A Study on the Table Design for Utilization of Cornus controversa Laminated Wood Manufactured by Pressing and Heating
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
In this study domestic thinning and small diameter woods of Giant dogwood (Cornus controversa Hemsl) was used. To increase the utilizability of wood, the utilizability was proposed after manufacturing laminated wood by pressing and heating. The physical and mechanical characteristics of Laminated wood were investigated and the color change was measured, using a Chromaticity coordinates, after being pressed at 10% (45 mm), 20% (40 mm), 30% (35 mm) for 5 minutes, using Stopper, and then heated at 180°C for 6, 12, 24 and 48 hours. The results were as follows. Wood density, compressive strength, MOR, MOE are increased with increasing pressing rate but decreased as heating time is increased after pressing. However, Color change is clear, dimensional stability is improved after pressing and heating.
Abstract
In this study domestic thinning and small diameter woods of Giant dogwood (Cornus controversa Hemsl) was used. To increase the utilizability of wood, the utilizability was proposed after manufacturing laminated wood by pressing and heating. The physical and mechanical characteristics of Laminated wood were investigated and the color change was measured, using a Chromaticity coordinates, after being pressed at 10% (45 mm), 20% (40 mm), 30% (35 mm) for 5 minutes, using Stopper, and then heated at 180°C for 6, 12, 24 and 48 hours. The results were as follows. Wood density, compressive strength, MOR, MOE are increased with increasing pressing rate but decreased as heating time is increased after pressing. However, Color change is clear, dimensional stability is improved after pressing and heating.
참고문헌 (10)
- 김광모, "백합나무 열처리재의 물리 및 역학적 특성", 목재공학, 38(1), pp.17~26 (2010), 한국목재공학회
- 신랑호, "가열·재색변환처리 목재를 이용한 생활용품개발에 관한 연구", 한국가구학회지, 20(5), pp.457~466 (2009), 한국가구학회
- 윤승락, "한국산 유용수종의 목재성질", pp.208~368 (2008), 국립산림과학원
- 황성욱, "라디에타소나무 열압밀화 목재의 경도와 치수안정성 - 압체 온도와 시간의 영향 -", 목재공학, 39(3), pp.206~212 (2011), 한국목재공학회
- 김재성, "수입목재의 유통 구조분석", 산립과학논문집, 68, pp.78~89 (2005)
- 한국표준협회, "KS F 2198, 2203, 2206, 2208", ~ (2001)
- Belhta, P, "Effect of high temper- ature on the change in color, dimensional stabilith and mechamiacal properties of spruce wood", Holzfoschung, 57, pp.539~546 (2003)
- Esteves, B, "Influence of steam heating on the properties of pine (Pinus Pinaster) and eucalypt (Eucalypus globulus) wood", Wood Sci Technol, 41, pp.193~207 (2007)
- Ohsaki, H, "Vibrational Properties of Wetwood of Todomatsu (Abies sachalinensis) at High Temperature", Hokkaido Forest Products Research Institute, 22(1), pp.19~23 (2008)
- Kollman. F. F. P, "Principles of wood science and technology" (1968), Springer Verlag