상압건조 나노다공성 실리카 에어로젤에 대한 용매의 영향
Influence of solvent on the nano porous silica aerogelsprepared by ambient drying process
1
조회
0
다운로드
3
인용
0
참고문헌
초록
Abstract
Nano porous, transparent silica aerogels monoliths were prepared under ambient drying (1 atm, 270oC) condition byhexane, n-heptane and xylene, were selected in the point view of low surface tension and vapor pressure in order to restraina formation of cracks during drying. Crack-free silica aerogels with over 93 % of porosity and below 0.14 g/cm3 of densitywere obtained by solvent exchange and surface modification under atmosphere condition. Optimum solvent was confirmedn-heptane among these solvents through estimation of FT-IR, TGA, BET and SEM. Modified silica aerogel exhibited ahigher porosity and pore size compare to unmodified aerogels. Hydrophobicity was also controled by C-H and H-OHbonding state in the gel structure and heat treatment over 400oC effects to the hydrophobicity due to oxidation of C-Hradicals.
참고문헌 (9)
- "Thin aerogel films for optical", 188, pp.46~53 (1995)
- "APSIS-aerogel position-sensitive impact sensor: Capabilities for in-situ collection and sample return", 25, pp.315~322 (2000)
- "실리카 에어로젤의 상압합성 및 특성연구", 33(12), pp.1394~1402 (1996)
- "실리카 에어로젤의 상압합성 및 특성연구", 36(11), pp.1189~1197 (1999)
- "Preparation of low-density aerogels at ambient pressure", 271, pp.567~572 (1992)
- "Silica aerogel film prepared at ambient pressure by using surface derivatization to induce reversible drying shrinkage", 374, pp.439~443 (1995)
- "Aerogels-highly tenuous solids with fascinating properties", 100, pp.169~ (1988)
- "Synthesis and characterization of low-dielectric silica aerogel films", 83(3), pp.533~ (2000)
- "상압건조 물유리 에어로젤에 대한 표면개질제의 영향", 15(3), pp.173~178 (2006)