Cumulative Damage Theory in Fatigue of Graphite/Epoxy [±45]s Composites
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The phenomenological evolution laws of damage can be defined either based on residual life or residual strength. The failure of a specimen can be defined immediately after or before fracture. The former is called in this paper by “failure defined by approach I” and the latter “failure defined by approach II.” Usually at failure there is a discontinuity of loading variables and, because of this, damage at failure is discontinuous. Therefore the values of damage at failure by two different approaches are not the same. Based on this idea the sequence effects of the phenomenological evolution law of damage given by dD/dN = g(D)f(Φ) were studied. Thin-walled graphite/epoxy tubes consisting of four of [±45]s laminates were used for the experimental study of sequence effects and the effects of mean stress on fatigue life. It was found that the sequence effects in two step uniaxial fatigue for [±45]s graphite/epoxy tubular specimen showed that a high-low block loading sequence was less damaging than a low-high one.
Abstract
The phenomenological evolution laws of damage can be defined either based on residual life or residual strength. The failure of a specimen can be defined immediately after or before fracture. The former is called in this paper by “failure defined by approach I” and the latter “failure defined by approach II.” Usually at failure there is a discontinuity of loading variables and, because of this, damage at failure is discontinuous. Therefore the values of damage at failure by two different approaches are not the same. Based on this idea the sequence effects of the phenomenological evolution law of damage given by dD/dN = g(D)f(Φ) were studied. Thin-walled graphite/epoxy tubes consisting of four of [±45]s laminates were used for the experimental study of sequence effects and the effects of mean stress on fatigue life. It was found that the sequence effects in two step uniaxial fatigue for [±45]s graphite/epoxy tubular specimen showed that a high-low block loading sequence was less damaging than a low-high one.
참고문헌 (23)
- Stephens, R. I, "Metal Fatigue in Engineering" (2001), John Wiley & Sons, Inc
- Krajcinovic, D, "Observations on Damage and Plasticity", Workshop on a Continuum Mechanics Approach to Damage and Life Prediction, pp.88~89 (1980)
- Lemaitre, J, "How to Use Damage Mechanics", Nuclear Engineering and Design, 80, pp.233~245 (1984)
- Palmgren, A.Z, "Die Lebensdauer von Kugellagern", Z. ver. Deutch, 68, pp.339~341 (1924)
- Miner, M.A, "Cumulative Damage in Fatigue", Journal of Applied Mechanics, 12, pp.A159~A164 (1945)
- Ben-Amoz, M, "Discussion of a Reinterpretation of the Palmgren-Miner Rule for Fatigue Life Prediction", Journal of Applied Mechanics, 48, pp.446~448 (1981)
- Yang, J.N, "Effect of Load Sequence on the Statistical Fatigue of Composites", AIAA, 18(12), pp.1525~1531 (1980)
- Hashin, Z, "A Cumulative Damage Theory of Fatigue Failure", Materials Science and Engineering, 34, pp.147~160 (1978)
- Hashin, Z, "A Reinterpretation of the Palmgren-Miner Rule for Fatigue Life Prediction", ASME Journal of Applied Mechanics, 47, pp.324~328 (1980)
- Subramanyan, S, "A Cumulative Damage Rule Based on the Knee Point of the S-N Curve", ASME Journal of Engineering Materials and Technology, 98, pp.316~321 (1976)
- A New Theory to Predict Cumulative Fatigue Damage in Fbierglass Reinforced Plastics, "Broutman, L.J", ASTM, 170~188, pp.ASTM STP 497 (1972)
- Bogganoff, J.L, "A New Cumulative Damage Model, Part 1", ASME Journal of Applied Mechanics, 45, pp.246~250 (1978)
- Hashin, Z, "Statistical Cumulative Damage Theory for Fatigue Life Prediction", ASME Journal of Applied Mechanics, 50, pp.571~579 (1983)
- Load Sequence Effects on the Fatigue of Unnotched Composite Materials, "Yang, J.N", ASTM, 213~232, pp.ASTM STP 723 (1981)
- Chou, P.C, "Modern Development in Composite Materials and Structure", pp.343~356 (1984), ASME
- Bengtsson, A, "Uncertainty in Fatigue Life Prediction of Structures Suject to Gaussian Loads", Probabilistic Engineering Mechanics, 24, pp.224~235 (2009)
- Rychlik, I, "Rain-flow fatigue Damage for Transformed Gaussian Loads", International Journal of Fatigue, 29, pp.406~420 (2007)
- Bui, H.D, "A Simplified Analysis of Creep Crack Growth Using Local Approach", International Seminar on Local Approach of Fracture, pp.373~388 (1986)
- Bui-Quoc, T, "An Engineering Approach for Cumulative Damage in Metals under Creep Loading", Journal of Engineering Materials and Technology, 101, pp.337~343 (1979)
- Paris, P.C, "A Critical Analysis of Crack Prop-agation Laws", ASME Journal of Basic Engineering, Ser. D, 85(3), pp.528~ (1963)
- Ostergren, W.J, "A Uniaxial Damage Accumulation Law for Time-Varying Loading Including Creep-Fatigue Interaction", ASME Journal of Pressure Vessel Technology, 101, pp.118~124 (1979)
- s Tubes, "Ph.D", Rensselaer Polytechnic Institute, 1983
- s Tubes, "Master", Rensselaer Polytechnic Institute, 1984