탄산화에 노출된 콘크리트 취약부의 확률론적 내구수명 평가
A Service Life Prediction for Unsound Concrete Under Carbonation Through Probability of Durable Failure
0
조회
0
다운로드
9
인용
0
참고문헌
키워드
초록
Generally, steel corrosion occurs in concrete structures due to carbonation in down-town area and underground site and it propagates to degradation of structural performance. In general diagnosis and inspection, only carbonation depth in sound concrete is evaluated but unsound concrete such as joint and cracked area may occur easily in a concrete member due to construction process. In this study, field survey of carbonation for RC columns in down-town area is performed and carbonation depth in joint and cracked concrete including sound area is measured. Probability of durable failure with time is calculated through probability variables such as concrete cover depth and carbonation depth which are obtained from field survey. In addition, service life of the structures is predicted based on the intended probability of durable failure in domestic concrete specification. It is evaluated that in a RC column, various service life is predicted due to local condition and it is rapidly decreased with insufficient cover depth and growth of crack width. It is also evaluated that obtaining cover depth and quality of concrete is very important because the probability of durable failure is closely related with C.O.V. of cover depth.
Abstract
Generally, steel corrosion occurs in concrete structures due to carbonation in down-town area and underground site and it propagates to degradation of structural performance. In general diagnosis and inspection, only carbonation depth in sound concrete is evaluated but unsound concrete such as joint and cracked area may occur easily in a concrete member due to construction process. In this study, field survey of carbonation for RC columns in down-town area is performed and carbonation depth in joint and cracked concrete including sound area is measured. Probability of durable failure with time is calculated through probability variables such as concrete cover depth and carbonation depth which are obtained from field survey. In addition, service life of the structures is predicted based on the intended probability of durable failure in domestic concrete specification. It is evaluated that in a RC column, various service life is predicted due to local condition and it is rapidly decreased with insufficient cover depth and growth of crack width. It is also evaluated that obtaining cover depth and quality of concrete is very important because the probability of durable failure is closely related with C.O.V. of cover depth.
참고문헌 (14)
- 권성준, "탄산화에 노출된 균열 콘크리트 구조물의 확률론적 내구설계", 대한토목학회 논문집A, 25(5A), pp.741~750 (2005), 대한토목학회
- 건설교통부, "콘크리트 표준시방서(내구성편)", 건설교통부, ~ (2004)
- 和泉意登志, "構造物の耐久性設計手法例一鐵筋のがぶり厚さの信賴性設計手法一", コンクリート工學, 26(11), pp.38~42 (1988)
- 阿部保彦, "ひび割れ幅がコンクリートの中性化深さに及ぼす影響に關する文獻調査結果", コンクリート構造物のリハビリテーシヨンに 關するシンポジウム論文集, pp.7~14 (1999)
- 和泉意登志, "コンクリートのひび割れ, 打継ぎ,豆板部たける中性化の進行", セメソト․コンクリート, (448), pp.50~55 (1984)
- 日本土木學會, "コンクリート構造物におけるコールドジヨイント問題と對策", 土木學會コンクリートライブ ラリー 103, (103) (2000)
- 和泉意登志, "中性化" (1986), 技報堂出版
- CEB, Thomas Telford, "Durable concrete structure-Design Code CEB, General Task Group 20", ~ (1989)
- CEB Task Group 5.1, 5.2, "New Approach to Durability Design, Sprint-Druck", ~ (1997)
- Gjorv, O. E., "Steel Corrosion in Concrete Structures Exposed to Norwegian Marine Environment", Concrete International, 16(4), pp.35~39 (1994)
- Gjorv, O. E., "Durability Design and Construction Quality of Concrete Structures", Proceedings of the 4th International Conference on Concrete, Seoul, Korea, CONSEC04, 통권 : 1, pp.44~55 (2004)
- Nawy,E.G., "Reinforced Concrete-A Fundamental Approach", pp.69~72 (1990), Prentice Hall,Inc.2nd Edition
- Durability Design of Concrete Structures, "RILEM", E&FN SPON, ~, pp.Technical Committee 130- CSL (1994)
- Service Life of Concrete Structures with regard to Corrosion of Reinforcement, "Vesikari,E", Technical Report Center of Finland, ~, pp.Technical Reports 533 (1988)