초기재령에서 각종 혼합콘크리트의 염소이온 고정화능력에 관한 연구

A Study on Chloride Binding Capacity of Various Blended Concretes at Early Age

이근주|송하원|이창홍
한국구조물진단유지관리공학회 (The Korea Institute For Structural Maintenance and Inspection)|2008.09|한국구조물진단유지관리공학회 논문집 (Journal of The Korea Institute for Structural Maintenance and Inspection)|제12권 제5호|pp. 133-143

1

조회

0

다운로드

4

인용

0

참고문헌

키워드

Corrosion resistance부식저항성염소이온혼합콘크리트Blended concrete고정화능력IsothermBinding capacityCholride
주제분류안전공학

초록

This paper studies the early-aged chloride binding capacity of various blended concretes including OPC(ordinary Portland cement), PFA(pulversied fly ash), GGBFS(ground granulated blast furnace slag) and SF(silica fume) cement paste. Cement pastes with 0.4 of a free water/binder ratio were cast with chloride admixed in mixing water, which ranged from 0.1 to 3.0% by weight of cement and different replacement ratios for the PFA, GGBFS and SF were used. The content of chloride in each paste was measured using water extraction method after 7 days curing. It was found that the chloride binding capacity strongly depends on binder type, replacement ratio and total chloride content. An increase in total chloride results in a decrease in the chloride binding, because of the restriction of the binding capacity of cement matrix. For the pastes containing maximum level of PFA(30%) and GGBFS(60%) replacement in this study, the chloride binding capacity was lower than those of OPC paste, and an increase in SF resulted in decreased chloride binding, which are ascribed to a latent hydration of pozzolanic materials and a fall in the pH of the pore solution, respectively. The chloride binding capacity at 7 days shows that the order of the resistance to chloride-induced corrosion is 30%PFA > 10%SF > 60%GGBFS > OPC, when chlorides are internally intruded in concrete. In addition, it is found that the binding behaviour of all binders are well described by both the Langmuir and Freundlich isotherms.

Abstract

This paper studies the early-aged chloride binding capacity of various blended concretes including OPC(ordinary Portland cement), PFA(pulversied fly ash), GGBFS(ground granulated blast furnace slag) and SF(silica fume) cement paste. Cement pastes with 0.4 of a free water/binder ratio were cast with chloride admixed in mixing water, which ranged from 0.1 to 3.0% by weight of cement and different replacement ratios for the PFA, GGBFS and SF were used. The content of chloride in each paste was measured using water extraction method after 7 days curing. It was found that the chloride binding capacity strongly depends on binder type, replacement ratio and total chloride content. An increase in total chloride results in a decrease in the chloride binding, because of the restriction of the binding capacity of cement matrix. For the pastes containing maximum level of PFA(30%) and GGBFS(60%) replacement in this study, the chloride binding capacity was lower than those of OPC paste, and an increase in SF resulted in decreased chloride binding, which are ascribed to a latent hydration of pozzolanic materials and a fall in the pH of the pore solution, respectively. The chloride binding capacity at 7 days shows that the order of the resistance to chloride-induced corrosion is 30%PFA > 10%SF > 60%GGBFS > OPC, when chlorides are internally intruded in concrete. In addition, it is found that the binding behaviour of all binders are well described by both the Langmuir and Freundlich isotherms.

참고문헌 (41)

  1. Glass, G.K., "Reinforced concrete-The principles of its deterioration and repair ; In Modern Matters-Principles and Practice in Conserving Recent Architecture", pp.101~112 (1996), Donhead Publishing
  2. Delagrave, A., "Chloride binding capacity of various hydrated cement paste systems", Adv. Cem. Mat, 6, pp.28~35 (1997)
  3. Mohammed, T.U., "between free chloride and total chloride contents in concrete", Cem. Concr. Res, 33, pp.1487~1490 (2003)
  4. Dhir, R.K., "Development of chloride-resisting concrete using fly ash", Fuel, 78, pp.137~142 (1999)
  5. Glass, G.K., "Neural network modelling of chloride binding", Mag. Concr. Res, 49, pp.323~335 (1997)
  6. Arya, C., "Factors influencing chloride-binding in concrete", Concr.Res, 20, pp.291~300 (1990)
  7. Suryavanshi, A.K., "Mechanism of Friedel's salt formation in cements rich in tri-calcium aluminate", Cem.Concr.Res, 26, pp.717~727 (1996)
  8. Xu, Y., "The influence of sulphates on chloride binding and pore solution chemistry", Concr.Res, 27, pp.1841~1850 (1997)
  9. Sandberg, P., "Studies of chloride binding in concrete exposed in a marine environment", Cem.Con.Res, 29, pp.473~477 (1999)
  10. Neville, A.M., "Properties of Concrete" (1995), Longman Group Ltd
  11. Hussain, S.E., "Factors affecting threshold chloride for reinforcement corrosionin concrete", Cem. Concr. Res, 25, pp.1543~1555 (1995)
  12. Suryavanshi, A.K., "The binding of chloride ions by sulphate resistant Portland cement", Cem.Concr.Res, 25, pp.581~592 (1995)
  13. Page, C.L., "The influence of different cements on chloride-induced corrosion of reinforcing steel", Cem.Concr.Res, 16, pp.79~86 (1986)
  14. Glass, G.K., "The influence of chloride binding on the chloride induced corrosion risk in reinforced concrete", Corros.Sci, 42, pp.329~344 (2000)
  15. Sandberg, P., "Studies of chloride binding in concrete exposed in a marine environment", Concr.Res, 29, pp.473~477 (1999)
  16. Arya, C., "Assessment of simple methods of determining the free chloride ion content of cement paste", Cem.Concr.Res, 17, pp.907~918 (1987)
  17. Sergi, G., "Diffusion of chloride and hydroxyl ions in cementitious materials exposed to a saline environment", Mag.Concr.Res, 44, pp.63~69 (1992)
  18. Page, C.L., "Diffusion of chloride ions in hardened cement pastes", Cem.Concr.Res, 11, pp.395~406 (1981)
  19. Dhir, R.K., "Chloride binding in GGBS concrete", Cem.Concr.Res, 26, pp.1767~1773 (1996)
  20. Condensed Silica Fume in Concrete: State of Art Report, "Thomas Telford", FIP, ~ (1988)
  21. Glass, G.K., "The presentation of the chloride threshold level for corrosion of steel in concrete", Corros.Sci, 39, pp.1001~1013 (1997)
  22. Tritthart, J., "Chloride binding: “II The influence of the hydroxide concentration in the pore solution of hardened cement paste on chloride binding", Cem.Concr.Res, 19, pp.683~691 (1989)
  23. Byfors, K., "Pore solution expression as a method to determine the influence of mineral additives on chloride binding", Cem.Concr.Res, 16, pp.760~770 (1986)
  24. ASTM C 1218, "Standard test method for water-soluble chloride in mortar and concrete American Society for Testing and Materials", ~ (1999)
  25. Ary, C., "An assessment of four methods of determining the free chloride content of concrete", Mater.Struct, 23, pp.319~330 (1990)
  26. Arya C., "Effect of cement type on chloride binding and corrosion of steel in concrete", Cem.Concr.Res, 25, pp.893~902 (1995)
  27. Lambert, P., "Investigations of reinforcement corrosion.2.Electrochemical monitoring of steel in chloride-contaminated concrete", Mater.Struct, 24, pp.351~358 (1991)
  28. Glass, G.K., "Process for the protection of reinforcement in reinforced concrete", International Patent Publication (2001)
  29. Song, H.W., "Chloride threshold level for steel corrosion in concrete", Corrosion Science, 49, pp.4113~4133 (2007)
  30. British Standard 8110, "Part 1. Structural use of concrete - Code of practice for design and construction", British Standards Institute, ~ (1985)
  31. Hansson, C.M., "The threshold concentration of chloride in concrete for initiation of reinforcement corrosion;In: Corrosion Rates of Steel in Concrete", pp.3~16 (1988), ASTM
  32. ACI Conference on Durability of Concrete, "Investigation on the threshold value of the critical chloride content;In: 4th CANMET", pp.1997, Breit, W.
  33. Ann, K.Y., "The influence of calcium nitrite on the initiation of chloride-induced corrosion of steel in concrete;n: Concrete under Sever Condition", pp.287~296 (2004), Consec
  34. Glass, G.K., "Corrosion inhibition in concrete arising from its acid neutralisation capacity", Corros. Sci, 42, pp.1587~1598 (2000)
  35. Hussain, S.E., "Corrosion resistance performance of fly ash blended cement concrete", ACI Mat. J, 91, pp.264~273 (1994)
  36. Song, H. W., "Factors influencing chloride transport in concrete structures exposed to a marine environment", Cem Concr Com, 30, pp.113~121 (2008)
  37. Song, H. W., "Chloride threshold value for steel corrosion in concrete considering the buffering capacity against a fall in the pH", ACI Mat J (2008)
  38. Ann, K.Y., "Build-up of surface chloride and its influence on corrosion initiation time of steel in concrete", EASEC-10,The Tenth East Asia-Pacific Conference on Structural Engineering & Construction,Thai,Bangkok, pp.265~274 (2006)
  39. Song, H. W., "Chloride binding isotherms in cement paste containing various binders", Life Cycle Management of Coastal Concrete Structues Conference.Nagaoka,Japan, pp.109~114 (2006)
  40. Song, H. W., "Development of chloride binding capacity in cement pastes and the influencing of the pH of hydration products", J. Can Civ Eng (2008)
  41. Song, H. W., "Service life prediction of concrete structures under marine environment considering coupled deterioration", ResBuildMon, 12(4), pp.265~284 (2006)

관련 논문AI추천

Corrosion of Steel in Blended Concretes containing OPC, PFA, GGBS and SF송하원, 이근주, 이창홍한국재료부식학회 · CORROSION SCIENCE AND TECHNOLOGY2009 · 제8권 제5호Resistance of Cementitious Binders to Chloride Induced Corrosion of Embedded Steel by Electrochemical and Microstructural Studies송하원, 안기용, Kim Tae Sang한국재료부식학회 · CORROSION SCIENCE AND TECHNOLOGY2009 · 제8권 제2호Resistance of Cementitious Binders Against a Fall in the pH at Corrosion Initiation송하원, 안기용, 이창홍, 정민선한국재료부식학회 · CORROSION SCIENCE AND TECHNOLOGY2009 · 제8권 제3호Prediction of Chloride Profile considering Binding of Chlorides in Cement Matrix송하원, 안기용, 이창홍한국재료부식학회 · CORROSION SCIENCE AND TECHNOLOGY2009 · 제8권 제2호활성화된 플라이애쉬 혼입콘크리트의 철근부식거동에 관한 전기화학적 연구송하원, 이근주, 이창홍, 벨루사라스와티한국구조물진단유지관리공학회 · 한국구조물진단유지관리공학회 논문집2008 · 제12권 제6호재령에 따른 고성능 콘크리트의 수화 특성치와 염화물 확산성 변화고태호, 권성준한국구조물진단유지관리공학회 · 한국구조물진단유지관리공학회 논문집2019 · 제23권 제6호

이 간행물의 다른 논문 (15건)

수중발파의 영향평가를 위한 Flow-Chart박선준, 박연수pp. 47-54터널 지보용 숏크리트의 유해이온에 대한 열화특성김동규, 정호섭pp. 55-64루프전달회복법(Loop Transfer Recovery: LTR)을 이용한 다자유도 DUOX 시스템의 지진동 제어이진호pp. 65-73무량판 구조시스템 접합부의 기둥 형상비에 따른 내진 성능 평가이현호, 천영수pp. 74-80UHPCC를 사용한 철근 콘크리트 보의 휨강도 평가박정준, 고경택, 강수태, 김성욱pp. 81-90
원문 보기