가스분무법에 의한 Fe계 비정질 분말의 제조와 볼밀링공정에 의한 연질 Cu분말과의 복합화 및 SPS 거동 (II) − II. 복합분말의 SPS와 특성 −
Production of Fe Amorphous Powders by Gas-Atomization Process and Subsequent Spark Plasma Sintering of Fe amorphous-ductile Cu Composite Powder Produced by Ball-milling Process (II) − II. SPS Behaviors of Composite Powders and their Characteristics −
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Fe based (Fe68.2C5.9Si 3.5B 6.7P 9.6Cr 2.1Mo2.0Al2.0) amorphous powder, which is a composition of iron blast cast slag, were produced by a gas atomization process, and sequently mixed with ductile Cu powder by a mechanical ball milling process. The Fe-based amorphous powders and the Fe-Cu composite powders were compacted by a spark plasma sintering (SPS) process. Densification of the Fe amorphous-Cu composited powders by spark plasma sintering of was occurred through a plastic deformation of the each amorphous powder and Cu phase. The SPS samples milled by AGO-2 under 500 rpm had the best homogeneity of Cu phase and showed the smallest Cu pool size. Micro-Vickers hardness of the as-SPSed specimens was changed with the milling processes.
Abstract
Fe based (Fe68.2C5.9Si 3.5B 6.7P 9.6Cr 2.1Mo2.0Al2.0) amorphous powder, which is a composition of iron blast cast slag, were produced by a gas atomization process, and sequently mixed with ductile Cu powder by a mechanical ball milling process. The Fe-based amorphous powders and the Fe-Cu composite powders were compacted by a spark plasma sintering (SPS) process. Densification of the Fe amorphous-Cu composited powders by spark plasma sintering of was occurred through a plastic deformation of the each amorphous powder and Cu phase. The SPS samples milled by AGO-2 under 500 rpm had the best homogeneity of Cu phase and showed the smallest Cu pool size. Micro-Vickers hardness of the as-SPSed specimens was changed with the milling processes.
참고문헌 (12)
- P. Duwez, , Progress in Solid state chemistry, 3, pp.377~ (1967)
- P. K. Rastogi, , J. Non-crystalline Solids, 5, pp.1~ (1970)
- W. L. Johnson, , Current Oponion in Solid State and Materials Science, 1, pp.383~ (1996)
- A. Inoue, , Acta Materialia., 48, pp.279~ (2000)
- M. Hagiwara, , Metal Trans. A, 13, pp.373~ (1982)
- H. Fu, , Scripta Mater., 52, pp.669~ (2005)
- C. C. Hays, , Mater. Sci. Eng. A, 304, pp.650~ (2001)
- Y. J. Kim, , Mater. Sci. Eng. A, 449, pp.1071~ (2007)
- 김진천, "연질 Cu 분말-가스분무 Ni계 벌크 비정질 복합분말의 방전플라즈마 소결에 관한 연구", 한국분말야금학회지, 13(5), pp.351~359 (2006), 한국분말야금학회
- D. V. Louzguine-Luzgin, , J. Alloys and Compounds, 483, pp.78~ (2009)
- H. Li, , Mater. Sci. Eng. A, 449, pp.189~ (2007)
- H. J. Ryu, (2009), J. Korean Powder Metall. Inst., In press