Al-B-C 조제 β-SiC의 스파크 플라즈마 소결에 미치는 α-SiC seed 첨가 영향: 미세 구조 변화
Influence of α-SiC Seed Addition on Spark Plasma Sintering of β-SiC with Al-B-C: Microstructural Development
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The unique features of spark plasma sintering process are the possibilities of a very fast heating rate and a short holding time to obtain fully dense materials. β-SiC powder with 0, 2, 6, 10 wt% of α-SiC particles (seeds) and 4 wt% of Al-B-C (sintering aids) were spark plasma sintered at 1700-1850oC for 10min. The heating rate, applied pressure and sintering atmosphere were kept at 100oC/min, 40 MPa and a flowing Ar gas (500 CC/min). Microstructural development of SiC as function of seed content and temperature during spark plasma sintering was investigated quantitatively and statistically using image analysis. Quantitative image analyses on the sintered SiC ceramics were conducted on the grain size, aspect ratio and grain size distribution of SiC. The microstructure of SiC sintered up to 1700oC consisted of equiaxed grains. In contrast, the growth of large elongated SiC grains in small matrix grains was shown in sintered bodies at 1750oC and the plate-like grains interlocking microstructure had been developed by increasing sintering temperature. The introduction of α-SiC seeds into β-SiC accelerated the grain growth of elongated grains during sintering, resulting in the plate-like grains interlocking microstructure. In the α-SiC seeds added in β-SiC,the rate of grain growth decreased with α-SiC seed content, however, bulk density and aspect ratio of grains in sintered body increased.
Abstract
The unique features of spark plasma sintering process are the possibilities of a very fast heating rate and a short holding time to obtain fully dense materials. β-SiC powder with 0, 2, 6, 10 wt% of α-SiC particles (seeds) and 4 wt% of Al-B-C (sintering aids) were spark plasma sintered at 1700-1850oC for 10min. The heating rate, applied pressure and sintering atmosphere were kept at 100oC/min, 40 MPa and a flowing Ar gas (500 CC/min). Microstructural development of SiC as function of seed content and temperature during spark plasma sintering was investigated quantitatively and statistically using image analysis. Quantitative image analyses on the sintered SiC ceramics were conducted on the grain size, aspect ratio and grain size distribution of SiC. The microstructure of SiC sintered up to 1700oC consisted of equiaxed grains. In contrast, the growth of large elongated SiC grains in small matrix grains was shown in sintered bodies at 1750oC and the plate-like grains interlocking microstructure had been developed by increasing sintering temperature. The introduction of α-SiC seeds into β-SiC accelerated the grain growth of elongated grains during sintering, resulting in the plate-like grains interlocking microstructure. In the α-SiC seeds added in β-SiC,the rate of grain growth decreased with α-SiC seed content, however, bulk density and aspect ratio of grains in sintered body increased.
참고문헌 (44)
- L. J. Schioler, , Am. Ceram. Soc. Bull, 64, pp.268~ (1986)
- K. Yamada, "Silicon-Carbide Ceramics", pp.9~ (1998), Uchida Rokakuho Publishing Ltd
- M. Srinivasam, "Structural Ceramics" (1989), Academic Press
- W. L. Vaushn, , J. Am. Ceram. Soc, 73, pp.1540~ (1990)
- S. Prochazka, "Ceramics for High Performance Applications,Burke, Gorum and Katz", pp.239~ (1974), Brook Hill
- W. Bocker, , Powder Metal. Inter, 10, pp.87~ (1976)
- D. H. Stutz, , J. Am. Ceram.Soc, 68, pp.479~ (1985)
- A. H. Heuer, , J. Am. Ceram. Soc, 61, pp.406~ (1978)
- L. U. Ogbuji, , J. Am.Ceram. Soc, 64, pp.91~ (1981)
- M. Omori, , J. Am. Ceram. Soc, 65, pp.92~ (1982)
- M. A. Mulla, , Acta Metall. Mater, 42, pp.303~ (1994)
- M. A. Mulla, , Am. Ceram. Soc. Bull, 70, pp.439~ (1991)
- N. P. Padture, , J. Am. Ceram. Soc, 77, pp.519~ (1994)
- S. H. Kim, , J. Mater. Sci, 38, pp.1117~ (2003)
- N. P. Padture, , J. Am. Ceram. Soc, 77, pp.2518~ (1994)
- Y. W. Kim, , Kor. J. Ceram, 2, pp.39~ (1996)
- Y. W. Kim, , J. Am.Ceram. Soc, 80, pp.99~ (1997)
- R. M. Williams, , Am. Ceram. Soc. Bull, 64, pp.1385~ (1985)
- B.-W. Lin, , J. Am.Ceram. Soc, 69, pp.67~ (1986)
- S. Shinozaki, , J. Am. Ceram.Soc, 64, pp.1389~ (1985)
- J. J. Cao, , J. Am. Ceram. Soc, 79, pp.461~ (1996)
- W. J. Moberlychan, , Acta Mater, 46, pp.1625~ (1998)
- W. J. Moberlychan, , Acta Mater, 46, pp.2471~ (1998)
- D. Chen, , Acta Mater, 48, pp.4599~ (2000)
- X. F. Zhang, , Acta Mater, 51, pp.3849~ (2003)
- X. F. Zhang, , J. Am. Ceram. Soc, 86, pp.1370~ (2003)
- M. Tokita, , J. Soc. Powder Technol. Jpn, 30, pp.790~ (1993)
- N. Tamari, , J. Ceram. Soc. Jpn, 103, pp.740~ (1995)
- T. Nishimura, , J. Mater. Sci. Lett, 14, pp.1046~ (1995)
- D. S. Perera, , J. Euro.Ceram. Soc, 18, pp.401~ (1998)
- Y. Zhou, , J.Mater. Res, 14, pp.3363~ (1999)
- S. W. Wang, , J. Mater. Res, 15, pp.982~ (2000)
- Y. Zhou, , J.Am. Ceram. Soc, 83, pp.654~ (2000)
- K.-S. Cho, , J. Kor. Ceram. Soc, 38, pp.687~ (2001)
- L. Gao, , J. Euro. Ceram. Soc, 22, pp.785~ (2002)
- K.-S. Cho, , J. Kor. Ceram. Soc., 40, pp.751~ (2003)
- W. Chen, , Mater. Sci. & Engineer, 394, pp.132~ (2005)
- U. Anselmi-Tamburini, , Mater. Sci. & Eng, 394, pp.139~ (2005)
- K.-S. Cho, , Key Eng. Mater, 287, pp.335~ (2005)
- K.-S. Cho, , J. Kor. Ceram. Soc., 42, pp.567~ (2005)
- Kyeong-Sik Cho, "Microstructure of spark plasma sintered silicon carbide with Al-B-C", Journal of Ceramic Processing Research, 9(5), pp.500~505 (2008), 세라믹공정연구센터
- Y.-W. Kim, , J. Mater.Res, 14, pp.4291~ (1999)
- K. Vanmeensel, , Acta Mater, 53, pp.4379~ (2005)
- Y.-W. Kim, , J. Euro. Ceram.Soc, 22, pp.1031~ (2002)