밀링조건이 사용 후 PDP패널의 유가금속 용출효율에 미치는 영향
The Effect of Milling Conditions for Dissolution Efficiency of Valuable Metals from PDP Waste Panels
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, the microstructure and valuable metals dissolution properties of PDP waste panel powders were investigated as a function of milling parameters such as ball diameter size, milling time, and rotational speed during high-energy milling process. The complete refinement of powder could achieved at the ball diameter size of 5 mm due to sufficient impact energy and the number of collisions. With increasing milling time, the average particle size was rapidly decreased until the first 30 seconds, then decreased gradually about 3 μm at 3 minutes and finally, increased with presence of agglomerated particles of 35 μm at 5 minutes. Although there was no significant difference on the size of the particle according to the rotational speed from 900 to 1,100 rpm, the total valuable metals dissolution amount was most excellent at 1,100 rpm. As a result, the best milling conditions for maximum dissolving amount of valuable metals (Mg: 375 ppm, Ag 135 ppm, In: 17 ppm) in this research were achieved with 5 mm of ball diameter size, 3min of milling time, and 1,100 rpm of rotational speed.
Abstract
In this study, the microstructure and valuable metals dissolution properties of PDP waste panel powders were investigated as a function of milling parameters such as ball diameter size, milling time, and rotational speed during high-energy milling process. The complete refinement of powder could achieved at the ball diameter size of 5 mm due to sufficient impact energy and the number of collisions. With increasing milling time, the average particle size was rapidly decreased until the first 30 seconds, then decreased gradually about 3 μm at 3 minutes and finally, increased with presence of agglomerated particles of 35 μm at 5 minutes. Although there was no significant difference on the size of the particle according to the rotational speed from 900 to 1,100 rpm, the total valuable metals dissolution amount was most excellent at 1,100 rpm. As a result, the best milling conditions for maximum dissolving amount of valuable metals (Mg: 375 ppm, Ag 135 ppm, In: 17 ppm) in this research were achieved with 5 mm of ball diameter size, 3min of milling time, and 1,100 rpm of rotational speed.
참고문헌 (21)
- S. J. Hwang., , Ceramist, 9, pp.75~ (2006)
- 홍현선, "폐 LCD 재활용 기술 현황과 전망", 한국자원공학회지, 47(5), pp.619~627 (2010), 한국자원공학회
- H. S. Hong., , KIC News, 13(1), pp.10~ (2010)
- H. Takamichi., , Sharp Technical Journal, 92, pp.17~ (2005)
- J. Chen., , Chinese Journal of Rare Metals, 27(1), pp.101~ (2003)
- H. M. Lee., , J. Kor. Powder. Metall. Inst, 17, pp.88~ (2010)
- S. J. Hsieh., , Mater. Sci. Eng. B, 158, pp.82~ (2009)
- M. Turner., , Computer Law and Security Report, 23, pp.73~ (2007)
- K. Takahashi., , Metall. Trans. A, 40, pp.891~ (2009)
- J. Li., , Waste Management, 29, pp.2033~ (2009)
- K. S. Park., , Thermochimica Acta, 493, pp.105~ (2009)
- 김효섭, "고에너지 밀링으로 제조된 폐디스플레이 패널 분말의 밀링시간에 따른 인듐 용출특성", 한국분말야금학회지, 18(4), pp.378~384 (2011), 한국분말야금학회
- H. H. Hausner, "Hand book of Powder Metallurgy, second edition" (1982), Chemical Publishing
- Randall M. German, "Powder Metallurgy & particulate Materials Processing" (2005), Metal Powder Industries Federation
- 엄영랑, "고에너지볼밀을 이용한 PVA 고분자가 표면 코팅된 B4C 나노복합재 제조", 한국분말야금학회지, 16(2), pp.110~114 (2009), 한국분말야금학회
- W. K. Kang., , J. Alloys and Compd., 536S, pp.S45~ (2012)
- 송준우, "폐실리콘의 고에너지 밀링 과정에서 초기 입자 크기가 분말의 미세화에 미치는 효과", 한국분말야금학회지, 17(3), pp.242~250 (2010), 한국분말야금학회
- Melgardt M. de Villiers, , Int. J. Pharm, 136, pp.175~ (1996)
- C. H. Lee., , Waste Management, 33, pp.730~ (2013)
- R. J. Charles, , Trans. AIME, 203, pp.80~ (1957)
- M. Gao., , Powder Technol, 84, pp.101~ (1995)