Synthesis, Characterization and Functionalization of the Coated Iron Oxide Nanostructures
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The iron oxides nanoparticles and iron oxide with other compounds are of importance in fields including biomedicine, clinical and bio-sensing applications, corrosion resistance, and magnetic properties of materials, catalyst,and geochemical processes etc. In this work we describe the preparation and investigation of the properties of coated magnetic nanoparticles consisting of the iron oxide core and organic modification of the residue. These fine iron oxide nanoparticles were prepared in air environment by the co-precipitation method using of Fe2+: Fe3+ where chemical precipitation was achieved by adding ammonia aqueous solution with vigorous stirring. During the synthesis of nanoparticles with a narrow size distribution, the techniques of separation and powdering of nanoparticles into rather monodisperse fractions are observed. This is done using controlled precipitation of particles from surfactant stabilized solutions in the form organic components. It is desirable to maintain the particle size within pH range, temperature,solution ratio wherein the particle growth is held at a minimum. The iron oxide nanoparticles can be well dispersed in an aqueous solution were prepared by the mentioned co-precipitation method. Besides the iron oxide nanowires were prepared by using similar method. These iron oxide nanoparticles and nanowires have controlled average size and the obtained products were investigated by X-ray diffraction, FESEM and other methods.
Abstract
The iron oxides nanoparticles and iron oxide with other compounds are of importance in fields including biomedicine, clinical and bio-sensing applications, corrosion resistance, and magnetic properties of materials, catalyst,and geochemical processes etc. In this work we describe the preparation and investigation of the properties of coated magnetic nanoparticles consisting of the iron oxide core and organic modification of the residue. These fine iron oxide nanoparticles were prepared in air environment by the co-precipitation method using of Fe2+: Fe3+ where chemical precipitation was achieved by adding ammonia aqueous solution with vigorous stirring. During the synthesis of nanoparticles with a narrow size distribution, the techniques of separation and powdering of nanoparticles into rather monodisperse fractions are observed. This is done using controlled precipitation of particles from surfactant stabilized solutions in the form organic components. It is desirable to maintain the particle size within pH range, temperature,solution ratio wherein the particle growth is held at a minimum. The iron oxide nanoparticles can be well dispersed in an aqueous solution were prepared by the mentioned co-precipitation method. Besides the iron oxide nanowires were prepared by using similar method. These iron oxide nanoparticles and nanowires have controlled average size and the obtained products were investigated by X-ray diffraction, FESEM and other methods.
참고문헌 (24)
- Sergey P. Gubin, "Magnetic Nanoparticles", pp.466~ (2009), WILEY-VCH
- Stepanka Klimkova., , Chemosphere, 82, pp.1178~ (2011)
- Alejandro Simón de Dios., "-", Anal. Chim. Acta, 666, pp.1~ (2010)
- A. Dyal., , J. Am. Chem. Soc, 125, pp.1684~ (2003)
- S. P. Gubin., , Russian Chemical Reviews, 74(6), pp.489~ (2005)
- Y. J. Song., , Mater. Lett, 64, pp.1789~ (2010)
- Miha Drofenik., , Mater. Lett, 65, pp.439~ (2011)
- Daniel Amara., , Colloids and Surfaces A : Physicochem. Eng. Aspects, 339, pp.106~ (2009)
- P. C. Morais., , Thin Solid Films, 515, pp.266~ (2006)
- J. S. Suh., , Biochemical and Biophysical Research Communications, 379, pp.669~ (2009)
- Yi, An., , Bioresour. Technol, 101, pp.9825~ (2010)
- M. J. Bonder., , J. Magn. Magn. Mater., 311, pp.658~ (2007)
- Di, Li., , Mater. Lett, 64, pp.2462~ (2010)
- Liying Zhang., "Fabrication and magnetic properties of Fe3O4 nanowire arrays in different diameters", J. Magn. Magn. Mater., 321, pp.L15~ (2009)
- N. Wang., "Growth of nanowires", Mater. Sci. Eng. R, 60, pp.1~ (2008)
- Qin Han., "Growth and Properties of Single-Crystalline g-Fe2O3 Nanowires", J. Phys. Chem. C, 111, pp.5034~ (2007)
- Q. Han., "Defects and growing mechanisms of a-Fe2O3 nanowires", Chem. Phys. Lett, 431, pp.100~ (2006)
- H. -W. Wang, , J. Magn. Magn. Mater, 310, pp.2425~ (2007)
- Ning Du., , Nanoscale Res Lett, 5, pp.1295~ (2010)
- Yong Ding., , Adv. Funct. Mater, 17, pp.1172~ (2007)
- R. Massart., , J. Magn. Magn. Mater, 149, pp.6~ (1995)
- Le Thi Mai Hoa., , J. Physics: Conference Series (Workshop on Advanced Materials Science and Nanotechnology (AMSN08), 187, pp.012~ (2009)
- Cullen T. Vogelson., , J. Non-Crystalline Solids, 290, pp.216~ (2001)
- Tran Trung., , Mater. Lett, 57, pp.2746~ (2003)