전자빔을 이용한 물리기상증착법으로 제조된 열차폐용4 mol% YSZ 코팅의 내열특성
Thermal Durability of 4YSZ Thermal Barrier Coating Deposited by Electron Beam PVD
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
4 mol% Yttria-stabilized zirconia (4YSZ) coatings with 200 μm thick are fabricated by Electron Beam Physical Vapor Deposition (EB-PVD) for thermal barrier coating (TBC). 150 μm of NiCrAlY based bond coat is prepared by conventional APS (Air Plasma Spray) method on the NiCrCoAl alloy substrate before deposition of top coating. 4 mol% YSZ top coating shows typical tetragonal phase and columnar structure due to vapor phase deposition process. The adhesion strength of coating is measured about 40 MPa. There is no delamination or cracking of coatings after thermal cyclic fatigue and shock test at 850oC.
Abstract
4 mol% Yttria-stabilized zirconia (4YSZ) coatings with 200 μm thick are fabricated by Electron Beam Physical Vapor Deposition (EB-PVD) for thermal barrier coating (TBC). 150 μm of NiCrAlY based bond coat is prepared by conventional APS (Air Plasma Spray) method on the NiCrCoAl alloy substrate before deposition of top coating. 4 mol% YSZ top coating shows typical tetragonal phase and columnar structure due to vapor phase deposition process. The adhesion strength of coating is measured about 40 MPa. There is no delamination or cracking of coatings after thermal cyclic fatigue and shock test at 850oC.
참고문헌 (25)
- C. G. Levi., , Curr. Opin. Solid State Mater. Sci, 8, pp.77~ (2012)
- D. R. Clarke., , Annu. Rev. Mater. Sci, 33, pp.383~ (2003)
- A. G. Evans., , J. Eur. Ceram. Soc, 28, pp.1405~ (2008)
- D. R. Clarke., , MRS. Bull, 37, pp.891~ (2012)
- W. Pan., , MRS. Bull, 37, pp.917~ (2012)
- S. I. Jung., , Surf. Coat. Tech, 204, pp.802~ (2009)
- K. V. Nissen., , J. therm. Spray. Technol, 20, pp.736~ (2011)
- S. Kuroda., , Thin Solid Films, 49, pp.200~ (1991)
- S. Sampath., , MRS. Bull, 37, pp.903~ (2012)
- B. K. Jang., , Surf. Coat. Technol, 207, pp.177~ (2012)
- M. Ohring., "Materials Science of Thin Films", pp.497~ (2001), Academic Press.
- A. F. Renteria., , Surf. Coat. Technol, 201, pp.2611~ (2006)
- X. Cao., , J. Eur. Ceram. Soc, 24, pp.1~ (2004)
- S. Krämer., , J. Am. Ceram. Soc, 91, pp.576~ (2008)
- R. Rajendran., , Eng. Fail. Anal, 26, pp.355~ (2012)
- U. Schulz., , Surf. Coat. Tech, 203, pp.449~ (2008)
- M. Seraffon., , Surf. Coat. Tech, 206, pp.1529~ (2011)
- R. G. Wellman., , Surf. Coat. Tech, 176, pp.253~ (2004)
- R. Vaßen., , Mater. Res. Soc. Bull, 37, pp.911~ (2012)
- 윤소영, "열차폐코팅용 La2Ce2O7-Gd2Ce2O7-Y2Ce2O7 Pyrochlore계의 고온 열전도도", 한국세라믹학회지, 44(7), pp.387~392 (2007), 한국세라믹학회
- K. S. Lee., , J. Alloys. Compd, 507, pp.448~ (2010)
- T. M. Pollock., , MRS. Bull, 37, pp.923~ (2012)
- R. D. Maier., , Am. Ceram. Soc. Bull, 60, pp.555~ (1981)
- L. Lelait., , J. Mater. Sci, 27, pp.5~ (1992)
- U. Schulz., , Int. J. Appl. Ceram. Technol, 1, pp.302~ (2005)