촉매 화학기상증착 공정에서 온도구배 설정을 통한 타이타늄 기판에서의 CNT 성장 거동
CNT Growth Behavior on Ti Substrate by Catalytic CVD Process with Temperature Gradient in Tube Furnace
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
In this study, modified catalytic chemical vapor deposition (CCVD) method was applied to control theCNTs (carbon nanotubes) growth. Since titanium (Ti) substrate and iron (Fe) catalysts react one another and form a newphase (Fe2TiO5) above 700oC, the decrease of CNT yield above 800oC where methane gas decomposes is inevitableunder common CCVD method. Therefore, we synthesized CNTs on the Ti substrate by dividing the tube furnace intotwo sections (left and right) and heating them to different temperatures each. The reactant gas flew through from theend of the right tube furnace while the Ti substrate was placed in the center of the left tube furnace. When the CNTgrowth temperature was set 700/950oC (left/right), CNTs with high yield were observed. Also, by examining the microstructureof CNTs of 700/950oC, it was confirmed that CNTs show the bamboo-like structure.
Abstract
In this study, modified catalytic chemical vapor deposition (CCVD) method was applied to control theCNTs (carbon nanotubes) growth. Since titanium (Ti) substrate and iron (Fe) catalysts react one another and form a newphase (Fe2TiO5) above 700oC, the decrease of CNT yield above 800oC where methane gas decomposes is inevitableunder common CCVD method. Therefore, we synthesized CNTs on the Ti substrate by dividing the tube furnace intotwo sections (left and right) and heating them to different temperatures each. The reactant gas flew through from theend of the right tube furnace while the Ti substrate was placed in the center of the left tube furnace. When the CNTgrowth temperature was set 700/950oC (left/right), CNTs with high yield were observed. Also, by examining the microstructureof CNTs of 700/950oC, it was confirmed that CNTs show the bamboo-like structure.
참고문헌 (18)
- A. C. Dupuis, , Prog. Mater. Sci., 50, pp.929~ (2005)
- M. S. Dresselhaus, , Phyl. Trans. R. Soc. Land. A, 362, pp.2065~ (2004)
- M. Paradise, , Mater. Design, 28, pp.1477~ (2007)
- A. Magrez, , Materials, 3, pp.4871~ (2010)
- J. W. Ward, , Chem. Phys. Lett., 376, pp.717~ (2003)
- A. Szabó, , Materials, 3, pp.3092~ (2010)
- A. N. Andriotti, , Phys. Rev. Lett., 85, pp.3193~ (2000)
- S. H. S. Zein, , Ind. Eng. Chem. Res., 43, pp.4864~ (2004)
- H. C. Lee, , Thin Solid Films, 616, pp.3646~ (2008)
- H. C. Zeng, , Curr. Opin. Chem. Eng., 1, pp.11~ (2011)
- F. Doustan, , J. Nanostructures, 3, pp.333~ (2013)
- T. Arcos, , J. Phys. Chem. B, 108, pp.7728~ (2004)
- B. Samira, , Res. J. Chem. Sci., 3, pp.62~ (2013)
- R. Vasquez, , Miner. Eng., 39, pp.99~ (2012)
- Ju Tack Han, "Synthesis of Carbon Nanotubes from Catalytic Decomposition of C2H2 through Pd", Al2O3 Catalysts, 2003, pp.24(12), 1771~1774[DOI]
- Y. Zhang, , J. Phys. Chem. C, 117, pp.24015~ (2013)
- F. Doustan, , J. Nanostructures, 3, pp.333~ (2013)
- R. Baker, , J. Catalysis, 37, pp.101~ (1975)