DyF3 paste 제조 및 이를 이용한 Nd-Fe-B 입계확산자석의 특성 연구
Synthesis of DyF3 paste and Magnetic Properties of GBDPed Nd-Fe-B Magnets
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Recently, the grain boundary diffusion process (GBDP), involving heavy rare-earth elements such as Dy and Tb, has been widely used to enhance the coercivity of Nd-Fe-B permanent magnets. For example, a Dy compound is coated onto the surface of Nd-Fe-B sintered magnets, and then the magnets are heat treated. Subsequently, Dy diffuses into the grain boundaries of Nd-Fe-B magnets, forming Dy-Fe-B or Nd-Dy-Fe-B. The dip-coating process is also used widely instead of the GBDP. However, it is quite hard to control the thickness uniformity using dip coating. In this study, first, a DyF3 paste is fabricated using DyF3 powder. Subsequently, the fabricated DyF3 paste is homogeneously coated onto the surface of a Nd-Fe-B sintered magnet. The magnet is then subjected to GBDP to enhance its coercivity. The weight ratio of binder and DyF3 powder is controlled, and we find that the coercivity enhances with decreasing binder content. In addition, the maximum coercivity is obtained with the paste containing 70 wt% of DyF3 powder.
Abstract
Recently, the grain boundary diffusion process (GBDP), involving heavy rare-earth elements such as Dy and Tb, has been widely used to enhance the coercivity of Nd-Fe-B permanent magnets. For example, a Dy compound is coated onto the surface of Nd-Fe-B sintered magnets, and then the magnets are heat treated. Subsequently, Dy diffuses into the grain boundaries of Nd-Fe-B magnets, forming Dy-Fe-B or Nd-Dy-Fe-B. The dip-coating process is also used widely instead of the GBDP. However, it is quite hard to control the thickness uniformity using dip coating. In this study, first, a DyF3 paste is fabricated using DyF3 powder. Subsequently, the fabricated DyF3 paste is homogeneously coated onto the surface of a Nd-Fe-B sintered magnet. The magnet is then subjected to GBDP to enhance its coercivity. The weight ratio of binder and DyF3 powder is controlled, and we find that the coercivity enhances with decreasing binder content. In addition, the maximum coercivity is obtained with the paste containing 70 wt% of DyF3 powder.
참고문헌 (7)
- J. G. Lee, , J. Korean Powder Metall. Inst., 19, pp.151~ (2012)
- 이정구, "희토류 자원문제 해결을 위한 모터 및 영구자석 연구개발 동향", 한국자기학회지, 22(2), pp.58~65 (2012), 한국자기학회[DOI]
- D. N. Brown, , J. Phys. Condens. Matter., 26, pp.064202~ (2014)
- S. Hirosawa, , J. Magn. Soc. Jpn., 39, pp.85~ (2015)
- Tae-Hoon Kim, "Effect of Dy on the Microstructural and Magnetic Properties of an Nd-Fe-B Strip-Cast Alloy", Metals and Materials International, 17(2), pp.329~334 (2011), 대한금속·재료학회
- K. H. Bae, , J. Alloys Compd., 612, pp.183~ (2014)
- F. Vial, , J. Magn. Magn. Mater., 242, pp.1329~ (2002)