대면적 Fecralloy 코팅층의 표면 거침도 극대화를 위한 정전분무 및 열처리 공정 연구
Electrospray and Thermal Treatment Process for Enhancing Surface Roughness of Fecralloy Coating Layer on a Large Sized Substrate
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Fecralloy coating layer with large surface area is suitable for use as a filter media for efficient removal of hot gaseous pollutants exhausted from combustion processes. For uniform preparation of a Fecralloy coating layer with large surface area and strong adhesion to substrate, electrospray coating and thermal treatment processes are experimentally optimized in this study. A nano-colloidal solution with 0.05 wt% Fecralloy nanoparticles is successfully prepared. Optimized electrospraying conditions are experimentally discovered to prepare a uniform coating layer of Fecralloy nanocolloidal solution on a substrate. Drying the electrospray coated Fecralloy nano-colloidal solution layer at 120oC and subsequent heating at 600oC are the best post-treatment for enhancing the adhesion force and surface roughness of the Fecralloy coating layer on a substrate. An electrospray coating system, consisting of several multi-groove nozzles, is also experimentally confirmed as a reasonable device for uniform coating of Fecralloy nano-colloid on a large area substrate.
Abstract
Fecralloy coating layer with large surface area is suitable for use as a filter media for efficient removal of hot gaseous pollutants exhausted from combustion processes. For uniform preparation of a Fecralloy coating layer with large surface area and strong adhesion to substrate, electrospray coating and thermal treatment processes are experimentally optimized in this study. A nano-colloidal solution with 0.05 wt% Fecralloy nanoparticles is successfully prepared. Optimized electrospraying conditions are experimentally discovered to prepare a uniform coating layer of Fecralloy nanocolloidal solution on a substrate. Drying the electrospray coated Fecralloy nano-colloidal solution layer at 120oC and subsequent heating at 600oC are the best post-treatment for enhancing the adhesion force and surface roughness of the Fecralloy coating layer on a substrate. An electrospray coating system, consisting of several multi-groove nozzles, is also experimentally confirmed as a reasonable device for uniform coating of Fecralloy nano-colloid on a large area substrate.
참고문헌 (17)
- K. Ohno, , SAE world congress (2000)
- S. Ichikawa, , Ceramics, 38, pp.296~ (2003)
- N. Miyakawa, , SAE world congress (2003)
- J. Banhart, , Prog. Mater. Sci., 46, pp.559~ (2001)
- R. R. Unocic, , Mater. Sci. Eng. A, 483, pp.25~ (2008)
- C. J. Bennett, , Proc. R. Soc. Lond., A, 439, pp.465~ (1992)
- M. V. Twing, "Structured Catalysts and Reactors", pp.59~ (1998), Marcel Dekker Inc.
- P. Avila, , Chem. Eng. J., 109, pp.1~ (2005)
- 윤중열, "정전 분무 공정을 이용한 Fecralloy 나노 입자가 코팅된 Fecralloy Foil의 제조", 한국분말야금학회지, 18(6), pp.526~531 (2011), 한국분말야금학회
- C. H. Cho, , Coat. Tech., 201, pp.4847~ (2007)
- M. I. Lerner, , Mendeleev. Commun., 11, pp.4~ (2001)
- S. Dong, , Scripta Mater., 44, pp.17~ (2001)
- C. Cho, , Appl. Phys. Lett., 91, pp.141501~ (2007)
- V. S. Giria, , Mater. Lett., 58, pp.1047~ (2004)
- M. Cloupeau, , J. Electrostatics, 22, pp.135~ (1989)
- M. Cloupeau, , J. Electrostatics, 25, pp.165~ (1990)
- J. Fernández de la Mora, , J. Fluid Mech., 260, pp.155~ (1994)