SLM 공정으로 제작된 SKD61 공구강의 조형 특성에 관한 연구
A study about sculpture characteristic of SKD61 tool steel fabricated by selective laser melting(SLM) process
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, two types of SKD61 tool-steel samples are built by a selective laser melting (SLM) process using the different laser scan speeds. The characteristics of two kinds of SKD61 tool-steel powders used in the SLM process are evaluated. Commercial SKD61 tool-steel power has a flowability of 16.68 sec/50 g and its Hausner ratio is calculated to be 1.25 by apparent and tapped density. Also, the fabricated SKD61 tool steel powder fabricated by a gas atomization process has a flowability of 21.3 sec/50 g and its Hausner ratio is calculated to be 1.18. Therefore, we confirmed that the two powders used in this study have excellent flowability. Samples are fabricated to measure mechanical properties. The highest densities of the SKD61 tool-steel samples, fabricated under the same conditions, are 7.734 g/cm3 (using commercial SKD61 powder) and 7.652 g/cm3 (using fabricated SKD61 powder), measured with Archimedes method. Hardness is measured by Rockwell hardness testing equipment 5 times and the highest hardnesses of the samples are 54.56 HRC (commercial powder) and 52.62 HRC (fabricated powder). Also, the measured tensile strengths are approximately 1,721 MPa (commercial SKD61 powder) and 1,552 MPa (fabricated SKD61 powder),respectively.
Abstract
In this study, two types of SKD61 tool-steel samples are built by a selective laser melting (SLM) process using the different laser scan speeds. The characteristics of two kinds of SKD61 tool-steel powders used in the SLM process are evaluated. Commercial SKD61 tool-steel power has a flowability of 16.68 sec/50 g and its Hausner ratio is calculated to be 1.25 by apparent and tapped density. Also, the fabricated SKD61 tool steel powder fabricated by a gas atomization process has a flowability of 21.3 sec/50 g and its Hausner ratio is calculated to be 1.18. Therefore, we confirmed that the two powders used in this study have excellent flowability. Samples are fabricated to measure mechanical properties. The highest densities of the SKD61 tool-steel samples, fabricated under the same conditions, are 7.734 g/cm3 (using commercial SKD61 powder) and 7.652 g/cm3 (using fabricated SKD61 powder), measured with Archimedes method. Hardness is measured by Rockwell hardness testing equipment 5 times and the highest hardnesses of the samples are 54.56 HRC (commercial powder) and 52.62 HRC (fabricated powder). Also, the measured tensile strengths are approximately 1,721 MPa (commercial SKD61 powder) and 1,552 MPa (fabricated SKD61 powder),respectively.
참고문헌 (22)
- A. Ladewig, , Additive Manuf., 10, pp.1~ (2016)[DOI]
- M.J. Matthews, , Acta Mater., 114, pp.33~ (2016)[DOI]
- B. Cheng, , Addtive Manuf., 90, pp.1~ (2016)
- 김우성, "DED방식의 적층가공을 통한 금형으로의 응용사례 및 효과", 대한용접접합학회지, 32(4), pp.10~14 (2014), 대한용접접합학회
- T. Wohlers, "Wohlers Associates Inc.", 28~ (2014)
- P. Feng, , Construct Build Mater., 93, pp.486~ (2015)[DOI]
- L. Parry, , Additive Manuf., 12, pp.1~ (2016)[DOI]
- D. Herzog, , Acta Mater., 117, pp.371~ (2016)[DOI]
- 최중호, "적층 가공된 3차원 조형체의 치밀화에 미치는 단일 melt pool 형상의 영향", 한국분말재료학회지, 24(3), pp.187~194 (2017), 한국분말재료학회[DOI]
- R.O. GREY, , Powder Tech., 2, pp.323~ (1968)
- C.J. Etti, , Agric. Agric. Sci. Procedia., 2, pp.120~ (2014)
- D. Geldart, , China Particuology, 4, pp.104~ (2006)[DOI]
- 윤재철, "금속 3D 프린팅 공정 최적화를 통한 H13 공구강 조형체의 기계적 특성 향상", 한국분말재료학회지, 24(3), pp.195~201 (2017), 한국분말재료학회[DOI]
- L.J. Jallo, , Powder Tech., 204, pp.63~ (2010)[DOI]
- H.Y. Jung, , Mater. Des., 86, pp.703~ (2015)[DOI]
- A.J. Pinkerton, , Int. J. Adv. Manuf. Technol., 25, pp.471~ (2005)[DOI]
- Y. Meng, , J. Mater. Pro cess. Tech., 212, pp.1731~ (2012)[DOI]
- E.C. Abdullah, , Powder Tech., 102, pp.151~ (1999)[DOI]
- D. Geldart, , Powder Tech., 190, pp.70~ (2009)[DOI]
- G. Telasang, , Surf. Coat. Tech., 258, pp.1108~ (2014)[DOI]
- G. Petzow, "Metallographic Etching", pp.62~ (1978)