동결건조 공정에서 Tert-butyl alcohol 기공형성제가 텅스텐 다공체의 기공구조에 미치는 영향
Effect of Tert-Butyl Alcohol Template on the Pore Structure of Porous Tungsten in Freeze Drying Process
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
The effect of tert-butyl alcohol (TBA) as a freezing solvent on the pore structure of a porous tungsten body prepared by freeze-drying is analyzed. TBA slurries with a WO3 content of 10 vol% are prepared by mixing with a small amount of dispersant and binder at 30oC. The slurries are frozen at -25oC, and pores are formed in the frozen specimens by the sublimation of TBA during drying in air. After hydrogen reduction at 800oC and sintering at 1000oC, the green body of WO3 is completely converted to porous W with various pore structures. Directional pores from the center of the specimen to the outside are observed in the sintered bodies because of the columnar growth of TBA. A decrease in pore directionality and porosity is observed in the specimens prepared by long-duration drying and sintering. The change in pore structure is explained by the growth of the freezing solvent and densification.
Abstract
The effect of tert-butyl alcohol (TBA) as a freezing solvent on the pore structure of a porous tungsten body prepared by freeze-drying is analyzed. TBA slurries with a WO3 content of 10 vol% are prepared by mixing with a small amount of dispersant and binder at 30oC. The slurries are frozen at -25oC, and pores are formed in the frozen specimens by the sublimation of TBA during drying in air. After hydrogen reduction at 800oC and sintering at 1000oC, the green body of WO3 is completely converted to porous W with various pore structures. Directional pores from the center of the specimen to the outside are observed in the sintered bodies because of the columnar growth of TBA. A decrease in pore directionality and porosity is observed in the specimens prepared by long-duration drying and sintering. The change in pore structure is explained by the growth of the freezing solvent and densification.
참고문헌 (17)
- T. Fukasawa, , J. Am. Ceram. Soc, 84, pp.230~ (2001)
- S. Deville, , Adv. Eng. Mater, 10, pp.155~ (2008)
- S. -W. Yook, , Mater. Lett, 63, pp.1502~ (2009)
- T. Fukasawa, , J. Mater. Sci, 36, pp.2523~ (2001)
- W. L. Ki, , Int. Mater. Rev., 57, pp.37~ (2012)
- Y. -H. Koh, , J. Am. Ceram. Soc, 89, pp.3089~ (2006)
- K. Araki, , J. Am. Ceram. Soc, 87, pp.2014~ (2004)
- R. Chen, , J. Am. Ceram. Soc, 90, pp.3478~ (2007)
- D. F. Souza, , Mater. Charact, 96, pp.183~ (2014)
- M. -Q. Sun, , J. Mater. Sci, 54, pp.5224~ (2019)
- K. C. Jeon, , Int. J. Refract. Met. Hard Mater, 53, pp.32~ (2015)
- 이규휘, "산화물 복합분말 첨가 Camphene 슬러리의 동결건조 공정에 의한 Cu-Co 복합계 다공체 제조", 한국분말재료학회지, 27(3), pp.193~197 (2020), 한국분말재료학회
- M. Wiśniewska, , Powder Technol, 198, pp.258~ (2010)
- S. H. Hyun, , J. Mater. Sci. Lett, 19, pp.1863~ (2000)
- T. R. Wilken, , Metall. Trans., 7B, pp.589~ (1976)
- 김경록, "동결-젤 주조 공정 기반 삼차부틸알코올을 이용한 단일방향 기공구조를 가지는 이상인산칼슘 세라믹 지지체의 제조 및 특성평가", 한국세라믹학회지, 50(4), pp.263~268 (2013), 한국세라믹학회
- Y. Tang, , J. Eur. Ceram. Soc, 36, pp.1513~ (2016)