나노클레이의 합성 및 나노복합재로의 응용

Abstract

Layered silicate was synthesized at hydrothermal condition from silica adding to various materials. Nano-clay was synthesized by intercaltion of various amine compounds into synthetic layered silicate. The products were analysed by XRD, SEM, and FT-IR in order to examine the condition of synthesis and intercalation. From the results, it was confirmed that kaolinite was synthesized from precipitated silica and gibbsite at 220℃ during 10 days, and hetorite was synthesized from silica sol at 100℃ during 48 h. Na-Magadiite was synthesized from silica gel at 150℃ during 72 h, and Na-kenyaite was synthesized from silica gel at 160℃ during 84 h. Nano-clay was prepared using synthetic layered silicate intercalated with various amine compounds. Kenyaite was easily intercalated by various organic compounds, and has the highest basal-spacing value among other layered silicates. Basal-spacing was changed according to the length of alkyl chain of amine comopounds. Polymer can be easily intercalated by dispersion with large space of interlayer. Finally, epoxy/nano -clay nanocomposite can be easily prepared.