산화물 분산강화 동합금의 열처리에 따른 미세조직 및 기계적 특성

Abstract

The alumina dispersion-strengthened (DS) C15715 Cu alloy fabricated by a powder metallurgy route was annealed at temperatures ranging from 800℃ to 1000℃ in the air and in vacuum. The effect of the annealing on microstructural stability and room-temperature mechanical properties of the alloy was investigated. The microstructure of the cold rolled DS alloy remained stable until the annealing at 900℃ in the air and in vacuum. No recrystallization of original grains occurred, but the dislocation density decreased and newly formed subgrains were observed. The alloy annealed at 1000℃ in the air experienced recrystallization and grain growth took place, however annealing in vacuum at 1000℃ did not cause the microstructural change. The mechanical property of the alloy was changed slightly with the annealing if the microstructure remained stable. However, the strength of the specimen that was recrystallized decreased drastically.