Ti 분말 첨가가 TiO2 나노 분말의 성형성에 미치는 영향
The Effect of Ti Powder addition on Compaction Behavior of TiO2 Nano Powder
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The compaction response of TiO2 nano powders with an addition of Ti powders prepared by magnetic pulsed compaction and subsequent sintering processes was investigated. All kinds of different bulk exhibited an average shrinkage of about 12% for different MPCed pressure and sintering temperature, which were approximately 50% lower than those fabricated by general process (20%) and a maximum density of around 92.7% was obtained for 0.8GPa MPCed pressure and 1400℃ sintering temperature. The addition of Ti powder induced an increase in the formability and hardness of the sintered TiO2. But the lower densities were obtained on sintering with addition of over 10 (wt%) Ti powder due to generation of crack during sintering. Subsequently it was verified that the optimum compaction pressure in MPC and sintering temperature were 0.8GPa and 1400℃, respectively.
Abstract
The compaction response of TiO2 nano powders with an addition of Ti powders prepared by magnetic pulsed compaction and subsequent sintering processes was investigated. All kinds of different bulk exhibited an average shrinkage of about 12% for different MPCed pressure and sintering temperature, which were approximately 50% lower than those fabricated by general process (20%) and a maximum density of around 92.7% was obtained for 0.8GPa MPCed pressure and 1400℃ sintering temperature. The addition of Ti powder induced an increase in the formability and hardness of the sintered TiO2. But the lower densities were obtained on sintering with addition of over 10 (wt%) Ti powder due to generation of crack during sintering. Subsequently it was verified that the optimum compaction pressure in MPC and sintering temperature were 0.8GPa and 1400℃, respectively.
참고문헌 (11)
- J. H. Song, , J. Kor. Ceram. Soc., 37, pp.625~ (2000)
- G. H. Lee, , J. Kor. Inst. Met. & Mater., 9, pp.425~ (2003)
- A. Kumpmann, , Mater. Sci. Eng. A., 168, pp.165~ (1993)
- H. C. Park, , J. Kor. Ceram. Soc., 29, pp.489~ (1992)
- H. S. Kim, , J. Kor. Mater. Res, 18, pp.8~ (2008)
- 강래철, "자기펄스 가압성형법에 의한 알루미나 나노분말의 치밀화 및 특성 평가", 한국분말야금학회지, 15(1), pp.37~45 (2008), 한국분말야금학회
- W. H. Rhodes, , J. Am. Ceram. Soc., 64, pp.19~ (1981)
- F. W. Dynys, , J. Am. Ceram. Soc., 67, pp.596~ (1984)
- Y. L. Chen, , Br: J. Ceram. Trans., 88, pp.7~ (1989)
- Mehdi Mazaheri, , Ceram. Int., 35, pp.685~ (2009)
- J. H. Shin, , J. Ceram. Soc., 37, pp.856~ (2000)