유성 볼밀법을 이용한 탄소 도핑 가시광 활성 TiO2 광촉매 제조 및 이의 특성 평가
Preparation of C Doped TiO2 Photocatalyst Activating to Visible Irradiation and Investigation of Its Photocatalytic Activity
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
A carbon doped TiO2 (C-TiO2) photocatalyst, which shows good photocatalytic activity to Ultraviolet irradiation and visible irradiation, was successfully prepared by co-grinding of TiO2 with ethanol or Activated Carbon(C), followed by heat treatment at 200oC in air for 60 min. Ethanol and C were used as a representative agent of liquid and solid for carbon doping. Their influence on improving photocatalytic ability and carbon doping degree was studied with degradation of methyl orange and XPS analysis. The product prepared by co-grinding of TiO2 with Ethanol had Ti-C and C-O chemical bonds and showed higher photocatalytic activity than the product prepared by co-grinding of TiO2 with C, where just C-O chemical bond existed. As a result,mechanochemical route is useful to prepare a carbon doped TiO2 photocatalyst activating to visible irradiation,where the solid-liquid operation is more effective than solid-solid operation to obtain a carbon doped TiO2.
Abstract
A carbon doped TiO2 (C-TiO2) photocatalyst, which shows good photocatalytic activity to Ultraviolet irradiation and visible irradiation, was successfully prepared by co-grinding of TiO2 with ethanol or Activated Carbon(C), followed by heat treatment at 200oC in air for 60 min. Ethanol and C were used as a representative agent of liquid and solid for carbon doping. Their influence on improving photocatalytic ability and carbon doping degree was studied with degradation of methyl orange and XPS analysis. The product prepared by co-grinding of TiO2 with Ethanol had Ti-C and C-O chemical bonds and showed higher photocatalytic activity than the product prepared by co-grinding of TiO2 with C, where just C-O chemical bond existed. As a result,mechanochemical route is useful to prepare a carbon doped TiO2 photocatalyst activating to visible irradiation,where the solid-liquid operation is more effective than solid-solid operation to obtain a carbon doped TiO2.
참고문헌 (23)
- A. Linsebigler, , Chem. Rev, 95, pp.735~ (1995)
- M. R. Hoffmann, , Chem. Rev, 95, pp.69~ (1995)
- N. Serpone, "Photocatalysis:Fundamentals and Applications", pp.1989, Wiley
- A. Fujishima, , Nature, 37, pp.238~ (1972)
- B. Òregan, , Nature, 353, pp.737~ (1991)
- K. I. Hadjiivanov, , Chem. Soc.Rev, 25, pp.61~ (1996)
- A. Heller, , Acc. Chem. Res, 28, pp.503~ (1995)
- I. C. Kang, , Environ. Sci. Technol, 42, pp.3622~ (2008)
- E. Ukaji, , Appl.Sur. Sci, 254, pp.563~ (2007)
- D. W. Bahnemanna, , Appl. Catal. B; Environ, 36, pp.161~ (2002)
- S. U. M. Khan, , Science, 297, pp.2243~ (2002)
- I. C. Kang, , J. Photochem. Photobiol. A: Chem, 189, pp.232~ (2007)
- J. Wang, , J.Phys. Chem. Solid, 68, pp.189~ (2007)
- R. Asahi, , Science, 293, pp.269~ (2001)
- L. Lin, , Appl. Catal. B: Environ, 75, pp.52~ (2007)
- X. Hong, , Chem. Mater, 17, pp.1548~ (2005)
- M. S. ElEskandarany, , Appl. Phys. Lett, 70, pp.1697~ (1997)
- I. C. Kang, , Appl. Catalysis B: Environ, 80, pp.81~ (2008)
- Q. Zhang, , Handbook of Power Techn, 12, pp.509~ (2007)
- H. Irie, , J. Phys.Chem, 107, pp.5483~ (2003)
- M. Iwasaki, , J. Colloid Interface Sci, 224, pp.202~ (2000)
- J. Yang, , Appl. Sur. Sci, 253, pp.1988~ (2006)
- W. Ren, , Appl. Catal, 69, pp.138~ (2007)