In-situ 고온 딜라토미터를 이용한 탄화붕소의 소결거동 연구
A Study of the Sintering Behavior of Boron Carbide using In-situ High Temperature Dilatometer
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
A high temperature dilatometer attached to a graphite furnace is built and used to study the sintering behaviorof B4C. Pristine and carbon doped B4C compacts are sintered at various soaking temperatures and their shrinkage profilesare detected simultaneously using the dilatometer. Carbon additions enhance the sinterability of B4C with sinteringto more than 97% of the theoretical density, while pristine B4C compacts could not be sintered above 91% due to particlecoarsening. The shrinkage profiles of B4C reveal that the effect of carbon on the sinterability of B4C can be seenmostly below 1950°C. The high temperature dilatometer delivers very useful information which is impossible to obtainwith conventional furnaces.
Abstract
A high temperature dilatometer attached to a graphite furnace is built and used to study the sintering behaviorof B4C. Pristine and carbon doped B4C compacts are sintered at various soaking temperatures and their shrinkage profilesare detected simultaneously using the dilatometer. Carbon additions enhance the sinterability of B4C with sinteringto more than 97% of the theoretical density, while pristine B4C compacts could not be sintered above 91% due to particlecoarsening. The shrinkage profiles of B4C reveal that the effect of carbon on the sinterability of B4C can be seenmostly below 1950°C. The high temperature dilatometer delivers very useful information which is impossible to obtainwith conventional furnaces.
참고문헌 (18)
- R. M. German, "Sintering Theory and Practice" (1996), John Wiley & Sons
- W. D. Kingert, "Introduction to Ceramics" (1976), John Wiley & Sons
- W. E. Lee, "Ceramic Microstructures, Property Control by Pressing" (1992), Chapman & Hall
- H. Palmour, "Ceramic Microstructures ’76", pp.308~ (1977), Boulder, CO
- G. Agawal, , J. Mater. Res., 11, pp.671~ (1996)
- F. Thevenot, , J. Euro. Ceram. Soc., 6, pp.205~ (1990)
- R. Angers, , Ceram. Int., 10, pp.49~ (1984)
- G. A. Gogotsi, , J. Mater. Sci. Lett., 7, pp.814~ (1988)
- 채재홍, "일축 가압 소결법을 이용한 고밀도 탄화 붕소 제조 및 기계적 특성", 한국세라믹학회지, 46(1), pp.81~85 (2009), 한국세라믹학회
- V. Skorokho Jr., , J. Mater. Sci. Lett., 15, pp.1337~ (1996)
- C. H. Lee, , J. Mater. Sci., 27, pp.6335~ (1992)
- Y. Kanno, , J. Ceram. Soc. Jpn., 95, pp.1137~ (1987)
- Z. Zakhariev, , J. Mater. Sci. Lett, 7, pp.695~ (1988)
- H. Suzuki, , Yogyo Kyokai Shi, 87, pp.430~ (1979)
- K. A. Schwetz, , J. Less-Common. Met., 82, pp.37~ (1981)
- F. Thevenot, , J. Nucl. Mater., 152, pp.154~ (1988)
- R. F. Speyer, , J. Mater. Sci., 39, pp.6017~ (2004)
- Decomposition Characteristics of a Char-Forming Phenolic Polymer used for Ablative Composite, "G. F. Skys", NASA, ~, pp.TN D-3810 (1967)