슈퍼 커패시터를 위한 WS2-W-WC가 내장된 탄소나노섬유 복합체의 제조
Fabrication of WS2-W-WC Embedded Carbon Nanofiber Composites for Supercapacitors
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
WS2-W-WC embedded carbon nanofiber composites were fabricated by using electrospinning method for use in high-performance supercapacitors. In order to obtain optimum electrochemical properties for supercapacitors, WS2 nanoparticles were used as precursors and the amounts of WS2 precursors were controlled to 4 wt% (sample A) and 8 wt% (sample B). The morphological, structural, and chemical properties of all samples were investigated by means of field emission photoelectron spectroscopy, transmission electron microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy. These results demonstrated that the embedded phases of samples A and B were changed from WS2 to WS2-W-WC through carbothermal reaction during carbonization process. In particular, sample B presented high specific capacitance (~119.7 F/g at 5 mV/s), good high-rate capacitance (~60.5%), and superb cycleability. The enhanced electrochemical properties of sample B were explained by the synergistic effect of the using 1-D structure supports, increase of specific surface area, and improved conductivity from formation of W and WC phases.
Abstract
WS2-W-WC embedded carbon nanofiber composites were fabricated by using electrospinning method for use in high-performance supercapacitors. In order to obtain optimum electrochemical properties for supercapacitors, WS2 nanoparticles were used as precursors and the amounts of WS2 precursors were controlled to 4 wt% (sample A) and 8 wt% (sample B). The morphological, structural, and chemical properties of all samples were investigated by means of field emission photoelectron spectroscopy, transmission electron microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy. These results demonstrated that the embedded phases of samples A and B were changed from WS2 to WS2-W-WC through carbothermal reaction during carbonization process. In particular, sample B presented high specific capacitance (~119.7 F/g at 5 mV/s), good high-rate capacitance (~60.5%), and superb cycleability. The enhanced electrochemical properties of sample B were explained by the synergistic effect of the using 1-D structure supports, increase of specific surface area, and improved conductivity from formation of W and WC phases.
참고문헌 (20)
- 이두희, "스마트 그리드 에너지 저장시스템 슈퍼커패시터의 MWCNT", Super P 함량에 따른 전기 화학적 특성, 2010, pp.23(11), 843~847[DOI]
- G. Wang, , Chem. Soc. Rev., 41, pp.797~ (2012)
- Y. J. Lee, , ECS Solid State Lett., 4 (2015)
- S. M. Chen, , Int. J. Electrochem. Sci., 9, pp.4072~ (2014)
- R. Kotz, , Electrochim. Acta, 45, pp.2483~ (2000)
- F. Li, , Nanotechnology, 20, pp.455602~ (2009)
- Young-Ha Kim, "Roles of nanosized Fe_3O_4 on supercapacitive properties of carbon nanotubes", Current Applied Physics, 11(3), pp.462~466 (2011), 한국물리학회
- 이유진, "Electrochemical capacitor를 위한 Ru 나노입자가 담지 된 다공성 탄소 나노섬유의 제조", 한국재료학회지, 24(1), pp.37~42 (2014), 한국재료학회
- B. Hu, , Electrochem. Commun., 28, pp.75~ (2013)
- W. Liu, , Carbon, 45, pp.2759~ (2007)
- R. Koc, , J. Eur. Ceram. Soc., 20, pp.1859~ (2000)
- A. D. Paola, , J. Phys. Chem. B, 103, pp.8236~ (1999)
- G. A. Swift, , J. Mater. Sci., 36, pp.803~ (2001)
- J. C. Sánchez-López, , Surf. Coat. Technol., 204, pp.947~ (2009)
- G. Lim, , Wear, 257, pp.863~ (2004)
- G. H. An, , ECS Solid State Lett., 2, pp.33~ (2013)
- M. S. Park, , Angew. Chem., 119, pp.764~ (2007)
- G. H. An, , J. Power Sources, 272, pp.828~ (2014)
- J. Martin, , Meas. Sci. Technol., 24, pp.085601~ (2013)
- H. Chhina, , J. Power Sources, 164, pp.431~ (2007)