진공사출금형용 STS316L 금속 다공체 제조 및 기계적 특성
Fabrication and Mechanical Properties of STS316L Porous Metal for Vacuum Injection Mold
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, porous stainless steel (STS316L) sintered body was fabricated by powder metallurgy method and its properties such as porosity, compressive yield strength, hardness, and permeability were evaluated. 67.5Fe-17Cr- 13Ni-2.5Mo (wt%) powder was produced by a water atomization. The atomized powder was classified into size with under 45 μm and over 180 μm, and then they were compacted with various pressures and sintered at 1210oC for 1 h in a vacuum atmosphere. The porosities of sintered bodies could be obtained in range of 20~53% by controlling the compaction pressure. Compressive yield strength and hardness were achieved up to 268 MPa and 94 Shore D, respectively. Air permeability was obtained up to 79 l/min·cm2. As a result, mechanical properties and air permeability of the optimized porous body having a porosity of 25~40% were very superior to that of Al alloy.
Abstract
In this study, porous stainless steel (STS316L) sintered body was fabricated by powder metallurgy method and its properties such as porosity, compressive yield strength, hardness, and permeability were evaluated. 67.5Fe-17Cr- 13Ni-2.5Mo (wt%) powder was produced by a water atomization. The atomized powder was classified into size with under 45 μm and over 180 μm, and then they were compacted with various pressures and sintered at 1210oC for 1 h in a vacuum atmosphere. The porosities of sintered bodies could be obtained in range of 20~53% by controlling the compaction pressure. Compressive yield strength and hardness were achieved up to 268 MPa and 94 Shore D, respectively. Air permeability was obtained up to 79 l/min·cm2. As a result, mechanical properties and air permeability of the optimized porous body having a porosity of 25~40% were very superior to that of Al alloy.
참고문헌 (9)
- "Future of Automotive Design & Materials"[URL]
- "KURZ: Design Trends in Automotive Interiors"[URL]
- 유호석, "Cu 입자가 분산된 Al2O3 다공체의 제조 및 항균특성", 한국분말야금학회지, 21(1), pp.16~20 (2014), 한국분말야금학회
- 최진호, "슬러리 코팅 공정으로 제조된Fe 폼의 기공 특성에 미치는 Fe 및 Fe2O3 분말의 혼합 비율의 영향", 한국분말야금학회지, 21(4), pp.266~270 (2014), 한국분말야금학회
- 김세훈, "다공성 Al-Cu 소결체의 제조 및 통기성 평가", 대한금속·재료학회지, 52(10), pp.783~789 (2014), 대한금속·재료학회[DOI]
- "Plastic Mold Steel"[URL]
- R. M. German, "Handbook of Mathematical Relations in Particulate Materials Processing", pp.8~ (2008), John Willey & Son Inc.
- R. M. German, "Powder Metallurgy & Particulate Materials Processing", pp.92~ (2005), MPIF
- "ASM Handbook alloy phase diagrams", pp.1624~ (1992), ASM International