Manufacturing and Macroscopic Properties of Kinetic Spray Ni-Cr-Al-Y Coating Layer
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
This study attempts to manufacture a Ni-Cr-Al-Y coating layer using a kinetic spray process and investigates the microstructure and physical properties of the manufactured layer. The Ni-22Cr-10Al-1Y (wt.%) composition powder is used, and it has a spherical shape with an average diameter of 23.7 μm. Cu plate is used as the substrate. Optical microscope, X-ray diffraction, scanning electron microscope and Vickers hardness test are carried out to characterize the macroscopic properties of the coating layer. Furthermore, the coating layer underwent vacuum heat treatment at temperatures of 400oC and 600oC for 1 hour to check the effect of heat treatment temperature on the properties. The manufactured coating layer is 1.5 mm thick, and featured identical phases to those found in the powder. The porosity of the coating layer is measured at 2.99%, and the hardness is obtained at 490.57 Hv. The layer shows reduced porosity as heat treatment temperature increased, and hardness is reduced at 400oC but shows a slight increase at 600oC. Based on the findings described above, this study also discusses possible manufacturing methods for a Ni-Cr-Al-Y coating layer using the kinetic spray process.
Abstract
This study attempts to manufacture a Ni-Cr-Al-Y coating layer using a kinetic spray process and investigates the microstructure and physical properties of the manufactured layer. The Ni-22Cr-10Al-1Y (wt.%) composition powder is used, and it has a spherical shape with an average diameter of 23.7 μm. Cu plate is used as the substrate. Optical microscope, X-ray diffraction, scanning electron microscope and Vickers hardness test are carried out to characterize the macroscopic properties of the coating layer. Furthermore, the coating layer underwent vacuum heat treatment at temperatures of 400oC and 600oC for 1 hour to check the effect of heat treatment temperature on the properties. The manufactured coating layer is 1.5 mm thick, and featured identical phases to those found in the powder. The porosity of the coating layer is measured at 2.99%, and the hardness is obtained at 490.57 Hv. The layer shows reduced porosity as heat treatment temperature increased, and hardness is reduced at 400oC but shows a slight increase at 600oC. Based on the findings described above, this study also discusses possible manufacturing methods for a Ni-Cr-Al-Y coating layer using the kinetic spray process.
참고문헌 (8)
- C. Zhou, , Surf. Coat. Technol., 161, pp.86~ (2002)
- A. R. Nicoll, , Mater. Sci. Technol., 2, pp.214~ (1986)
- T. H. Van Steenkiste, , Key Eng. Mater., 197, pp.59~ (2001)
- R. C. McCune, , J. Therm. Spray Technol., 9, pp.73~ (2000)
- Q. Zhang, , Surf. Coat. Technol., 202, pp.3378~ (2008)
- T. Stoltenhoff, , Coat. Technol., 200, pp.4947~ (2006)
- C. J. Li, , J. Therm. Spray Technol., 15, pp.212~ (2006)
- X. M. Peng, , Mater. Chem. Phys., 107, pp.158~ (2008)