방전 플라즈마 소결(Spark Plasma Sintering) 방법에 의해 제조된 Nb-Si-B계 합금의 미세조직 특성
Microstructure Characterization of Nb-Si-B alloys Prepared by Spark Plasma Sintering Process
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Microstructural examination of the Nb-Si-B alloys at Nb-rich compositions is performed. The Nb-rich corner of the Nb-Si-B system is favorable in that the constituent phases are Nb (ductile and tough phase with high melting temperature) and T2 phase (very hard intermetallic compound with favorable oxidation resistance) which are good combination for high temperature structural materials. The samples containing compositions near Nb-rich corner of the Nb- Si-B ternary system are prepared by spark plasma sintering (SPS) process using T2 and Nb powders. T2 bulk phase is made in arc furnace by melting the Nb slug and the Si-B powder compact. The T2 bulk phase was subsequently ballmilled to powders. SPS is performed at 1300oC and 1400oC, depending on the composition, under 30 MPa for 600s, to produce disc-shaped specimen with 15 mm in diameter and 3 mm high. Hardness tests (Rockwell A-scale and micro Vickers) are carried out to estimate the mechanical property.
Abstract
Microstructural examination of the Nb-Si-B alloys at Nb-rich compositions is performed. The Nb-rich corner of the Nb-Si-B system is favorable in that the constituent phases are Nb (ductile and tough phase with high melting temperature) and T2 phase (very hard intermetallic compound with favorable oxidation resistance) which are good combination for high temperature structural materials. The samples containing compositions near Nb-rich corner of the Nb- Si-B ternary system are prepared by spark plasma sintering (SPS) process using T2 and Nb powders. T2 bulk phase is made in arc furnace by melting the Nb slug and the Si-B powder compact. The T2 bulk phase was subsequently ballmilled to powders. SPS is performed at 1300oC and 1400oC, depending on the composition, under 30 MPa for 600s, to produce disc-shaped specimen with 15 mm in diameter and 3 mm high. Hardness tests (Rockwell A-scale and micro Vickers) are carried out to estimate the mechanical property.
참고문헌 (13)
- B. P. Bewlay, , Metal. Mater. Trans. A., 34, pp.2043~ (2003)
- V. Behrani, , Intermetallics, 14, pp.24~ (2006)
- T. Murakami, , Intermetallics, 7, pp.1043~ (1999)
- Z. Li, , Mater. Lett., 62, pp.2229~ (2008)
- R. Sakidja, , Acta Mater., 56, pp.5223~ (2008)
- J. M. Byun, , Int. J. Refract. Met. Hard Mater., 53, pp.61~ (2015)
- S. H. Hwang, , J. Alloys Compd., 585, pp.418~ (2014)
- K. C. G. Candioto, , Mater. Char., 47, pp.241~ (2001)
- S. Katrych, , J. Solid State Chem., 177, pp.493~ (2004)
- J. -M. Joubert, , J. Solid State Chem., 190, pp.111~ (2012)
- 주수현, "Nb-Si-B계에서 Nb+T2 공존 영역의 미세조직 특성", 대한금속·재료학회지, 53(1), pp.43~50 (2015), 대한금속·재료학회[DOI]
- C. A. Nunes, , J. Phase Equil. Diff., 32, pp.92~ (2011)
- M. E. Schlesinger, , J. Phase Equil., 15, pp.90~ (1994)