10 wt%, 20 wt%Li-TiO2 복합분말의 합성과 광촉매 활성평가
Synthesis and Photo Catalytic Activity of 10 wt%, 20 wt%Li-TiO2 Composite Powders
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
10 wt.% and 20 wt.%Li-TiO2 composite powders are synthesized by a sol-gel method using titanium isopropoxide and Li2CO3 as precursors. The as-received amorphous 10 wt.%Li-TiO2 composite powders crystallize into the anatase-type crystal structure upon calcination at 450oC, which then changes to the rutile phase at 750oC. The asreceived 20 wt%Li-TiO2 composite powders, on the other hand, crystallize into the anatase-type structure. As the calcination temperature increases, the anatase TiO2 phase gets transformed to the LiTiO2 phase. The peaks for the samples obtained after calcination at 900oC mainly exhibit the LiTiO2 and Li2TiO3 phases. For a comparison of the photocatalytic activity, 10 wt.% and 20 wt.% Li-TiO2 composite powders calcined at 450oC, 600oC, and 750oC are used. The 20 wt.%Li-TiO2 composite powders calcined at 600oC show excellent efficiency for the removal of methylorange.
Abstract
10 wt.% and 20 wt.%Li-TiO2 composite powders are synthesized by a sol-gel method using titanium isopropoxide and Li2CO3 as precursors. The as-received amorphous 10 wt.%Li-TiO2 composite powders crystallize into the anatase-type crystal structure upon calcination at 450oC, which then changes to the rutile phase at 750oC. The asreceived 20 wt%Li-TiO2 composite powders, on the other hand, crystallize into the anatase-type structure. As the calcination temperature increases, the anatase TiO2 phase gets transformed to the LiTiO2 phase. The peaks for the samples obtained after calcination at 900oC mainly exhibit the LiTiO2 and Li2TiO3 phases. For a comparison of the photocatalytic activity, 10 wt.% and 20 wt.% Li-TiO2 composite powders calcined at 450oC, 600oC, and 750oC are used. The 20 wt.%Li-TiO2 composite powders calcined at 600oC show excellent efficiency for the removal of methylorange.
참고문헌 (10)
- 이상훈, "양극산화된 TiO2 및 WO3 나노구조체로 구성된 광전기변색 소자 제작", 한국분말야금학회지, 22(5), pp.326~330 (2015), 한국분말야금학회
- 김지영, "광화학 환원방법을 이용한 Pt@TiO2 나노 복합체 합성", 한국분말야금학회지, 21(2), pp.119~123 (2014), 한국분말야금학회
- 여인철, "가시광 활성 WO3-TiO2 복합체 광촉매의 제조 및 이의 특성 평가", 한국분말야금학회지, 20(6), pp.474~478 (2013), 한국분말야금학회
- J. Ma, , Appl. Catal. B-Environ., 179, pp.21~ (2015)
- Y. Liu, , Appl. Surf. Sci., 315, pp.314~ (2014)
- B. T. Lee, , Mater. Lett., 60, pp.2101~ (2006)
- J. K. Han, , Mater. Lett., 61, pp.3798~ (2007)
- D. Das, , J. Mol. Catal. A-chem., 189, pp.271~ (2002)
- 한재길, "나노 결정립 TiO2-SrO 복합분체의 합성과 가시광 광촉매 활성평가", 대한금속·재료학회지, 45(8), pp.484~488 (2007), 대한금속·재료학회
- J. Xie, , Mater. Lett., 110, pp.57~ (2013)